Synthesis of the Micro-meso Porous SiO2 Xerogel and Its Physicochemical Properties

Sun Siyuan,Ge Yiyao,Tian Zhaobo,Zhang Jie,Xie Zhipeng

2018-01-01

Rare Metal Materials and Engineering

Abstract:Monodisperse nano-SiO2 particles were obtained via a novel improved Stober method, and the micro-meso porous SiO2 xerogels were further obtained after drying in air. The nano-SiO2 particles with the average size of 23 nm, exhibit good dispersibility in alcohol. The as-obtained amorphous SiO2 xerogels are featured with Si-OH and Si-OR groups on the surface, implying an incomplete hydrolysis and condensation process. Meanwhile, a large number of defects are remained inside and on the surface of the SiO2 xerogels, thus displaying good photoluminescence behaviors. The ultraviolet (lambda(em) = 355 nm) fluorescence under lambda(ex) = 300 nm excitation as well as the visible light (lambda(em) = 430 nm) phosphorescent under lambda(ex) = 380 nm excitation is observed in the as-obtained SiO2 xerogels. The calculated results according to N-2 sorption isotherms demonstrate that specific surface area of the SiO2 xerogels is 559 m(2)/g, the pore volume is 0.62 cm(3)/g and a large number of micropores and mesopores exist in the SiO2 xerogels.