Abstract:Interconnects in very large scale integration (VLSI) chips are susceptible to failure due to stress migration (SM) and electromigration (EM). At use condition, these two failure mechanisms play a collective role in causing interconnect failure. We present a study on SM and EM interaction in lower (MX structure) and upper metal (MX+1 structure) of dual-damascene Cu/low-κ interconnects. It is found that both mechanisms are dependent; statistical analysis shows that EM failure time is affected by the presence of residual stress induced by SM. This effect was more severe in the lower metal, where the EM median-time-to-failure (t50) for the majority of samples could be degraded by 30%–60%. For the upper metal of Cu interconnects, the t50 is degraded by about 10%. The reliability implication of the residual stress in copper interconnects on the EM is further investigated with various failure analysis techniques and three-dimensional finite element simulation. It is proposed that SM can influence EM when there is significant amount of vacancy accumulation due to SM in the cathode area which accelerates EM nucleation time. In the case of the MX structure, our experimental results show that SM and EM interaction occurs exactly below the via at the MX cathode side, leading to abrupt failures. On the other hand, in MX+1 structure, vacancies are likely to accumulate at the edge of upper metal lead during SM test, thus accelerating the failure during subsequent EM test. A failure mechanism model for stress evolution and void formation is proposed to provide insight into the interaction between these two failure mechanisms.

The Effect of Line Width on Stress-Induced Voiding in Cu Dual Damascene Interconnects

Experimental and Numerical Studies of Stress Migration in Cu Interconnects Embedded in Different Dielectrics

Effect of leveler on microstructure and stress of electroplated copper for TSV application

Carbon Nanotube Vias: Does Ballistic Electron–Phonon Transport Imply Improved Performance and Reliability?

The effect of stress migration on electromigration in dual damascene copper interconnects

Impact of TSV Induced Thermo-Mechanical Stress on Semiconductor Device Performance

Stress modeling of Cu/low-k BEoL - application to stress migration

Simulation and experiments of stress migration for Cu/low-k BEoL

Comprehensive study of the impact of TSV induced thermo-mechanical stress on 3D IC device performance

Electromigration behavior of 60 nm dual damascene Cu interconnects

The Effect of Pressure and Orientation on Cu-Cu3Sn Interface Reliability under Isothermal Ageing and Monotonic Traction Via Molecular Dynamics Investigation

Interfacial Stress in Through Silicon Vias

Effects Of Via Pitch On Silicon Stress In Tsv Interposer

Electromigration-induced void evolution and failure of Cu/SiCN hybrid bonds

The Influences of Grain Size Distributions on Thermal-Stresses in Cu-TSV

On the origins of near-surface stresses in silicon around Cu-filled and CNT-filled through silicon vias

A Molecular Dynamics Investigation of the Effect of Pressure and Orientation on the Cu Consumption in Cu-Cu3Sn Interface under Isothermal Ageing and Its Dissipative Mechanisms during Traction

Finite Element Analysis of the Thermal-Hygroscopic Stress of the Through Silicon Vias(TSV) Interconnect Structure

The Effect Of Cu Orientation On Fracture Location In Cu3sn-Cu Interface Structure Under Monotonic Loading Condition By Molecular Dynamics Simulation

Self-consistent Design Issues for High Frequency Cu Interconnect Reliability Incorporating Skin Effect.

Comparison of the Time-Dependent Physical Processes in the Electromigration of Deep Submicron Copper and Aluminum Interconnects