An investigation on component and formation of tribochemical film in Si3N4-white iron sliding pair lubricated with distilled water
Yi-Min Gao,Liang Fang,Jun-Yi Su,Xue-Wu Xu
DOI: https://doi.org/10.1016/S0301-679X(97)00057-1
IF: 5.62
1997-01-01
Tribology International
Abstract:A tribofilm was formed during wear tests of a Si3N4-white iron pair lubricated with distilled water. In order to clarify the formation of the film, the wear tests for Si3N4-white iron pair with different sliding distances were carried out on a ring-block tester, using distilled water as lubricant. The worn surfaces of white iron specimens were observed under SEM. Furthermore, the component and structure of the film were analyzed by using AES, XPS, FTIR and XRD. From the investigation, the following results are presented. During the wear tests of Si3N4-white iron pair lubricated with distilled water, the oxidation and hydrolysis of Si3N4 occur on the wearing surfaces, and a tribochemical film, which mainly consists of silica gel, is formed on the wearing surface. The reason for the film formation is that the carbides in cast iron spall off during the wearing tests and the spalling pits are left on the wearing surface of the white iron. Then, the debris of Si3N4 or its oxidized product are embedded into the pits, and are further oxidized and hydrolyzed. The products of reactions are concentrated in the pits and polycondensed into silica gel, and a silica gel film is formed on the wearing surface. The film protects both Si3N4 and white iron, and makes the paired surfaces smooth. Therefore, the friction coefficient of the pair is down to 0.02, and the wear rates of Si3N4 and iron are near zero. However, because the resultants of oxidation and hydrolysis of Si3N4 can not be enriched on the wearing surface of carbon steel to form an effective tribofilm, both friction coefficient and wear rate of Si3N4-carbon steel pair lubricated with distilled water are still high in value. (C) 1998 Elsevier Science Ltd.