Abstract:The facile synthesis of highly ordered mesoporous aluminas with high thermal stability and tunable pore sizes is systematically investigated. The general synthesis strategy is based on a sol-gel process associated with nonionic block copolymer as templates in ethanol solvent. Small-angle XRD, TEM, and nitrogen adsorption and desorption results show that these mesoporous aluminas possess a highly ordered 2D hexagonal mesostructure, which is resistant to high temperature up to 1000 degrees C. Ordered mesoporous structures with tunable pore sizes are obtained with various precursors, different acids as pH adjustors, and different block copolymers as templates. These mesoporous aluminas have large surface areas (ca. 400 m(2)/g), pore volumes (ca. 0.70 cm(3)/g), and narrow pore-size distributions. The influence of the complexation ability of anions and hydro-carboxylic acid, acid volatility, and other important synthesis conditions are discussed in detail. Utilizing this simple strategy, we also obtained partly ordered mesoporous alumina with hydrous aluminum nitrate as the precursor. FTIR pyridine adsorption measurements indicate that a large amount of Lewis acid sites exist in these mesoporous aluminas. These materials are expected to be good candidates in catalysis due to the uniform pore structures, large surface areas, tunable pore sizes, and large amounts of surface Lewis acid sites. Loaded with ruthenium, the representative mesoporous alumina exhibits reactant size selectivity in hydrogenation of acetone, D-glucose, and D-(+)-cellobiose as a test reaction, indicating the potential applications in shape-selective catalysis.

Preparation of Mesoporous Alumina and Its Application in Dehydration of Methanol to Dimethyl Ether

Synthesis of highly porous nanocrystalline alumina as a robust catalyst for dehydration of methanol to dimethyl ether

Synthesis of Dimethyl Ether Via Methanol Dehydration over Combined Al2o3-Hzsm-5 Solid Acids

Highly Dispersed CrOx Nanoparticle-Modified NaZSM-5 for Dehydration of Methanol to Dimethyl Ether

Hierarchical Mesoporous ZSM-5 for the Dehydration of Methanol to Dimethyl Ether

Reaction Kinetics of Methanol Dehydration over Combined AI203-HZSM-5 Solid Acids

Adsorption and Dehydration of Methanol on Al2o3 Catalyst

Micro-mesoporous Composite Molecular Sieves H-ZSM-5/MCM-41 for Methanol Dehydration to Dimethyl Ether: Effect of SiO2/Al2O3 Ratio in H-ZSM-5

Synthesis of γ-Al2O3–CeO2 catalyst with high surface area, high stability, and less coke formation for methanol dehydration reaction process

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Highly Dispersed Crox Nanoparticles Modified Nazsm-5 for Lower Temperature Dehydration of Methanol to Dimethyl Ether

Catalytic dehydration of methanol to dimethyl ether over micro–mesoporous ZSM-5/MCM-41 composite molecular sieves

The Morphologically Controlled Synthesis and Application of Mesoporous Alumina Spheres

Dehydration of Methanol to Dimethyl Ether over Al2(SO4)3/SiO2 Catalysts

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

PREPARATION OF AMORPHOUS AlO TEMPLATE

Regulating Surface Acid-Base Balance on NaZSM-5 by Fe Modification Towards Enhanced Methanol Dehydration to Dimethyl Ether

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

Catalytic performance of metal ion doped MCM-41 for methanol dehydration to dimethyl ether

Gas-Liquid Interfacial Deposition Synthesis of Alumina with Large Mesopores