Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Highly Dispersed Crox Nanoparticles Modified Nazsm-5 for Lower Temperature Dehydration of Methanol to Dimethyl Ether

Highly Dispersed CrOx Nanoparticle-Modified NaZSM-5 for Dehydration of Methanol to Dimethyl Ether

Regulating Surface Acid-Basic Balance on Nazsm-5 by Fe3+ Solution Towards Enhanced Methanol Dehydration

Regulating Surface Acid-Base Balance on NaZSM-5 by Fe Modification Towards Enhanced Methanol Dehydration to Dimethyl Ether

Micro-mesoporous Composite Molecular Sieves H-ZSM-5/MCM-41 for Methanol Dehydration to Dimethyl Ether: Effect of SiO2/Al2O3 Ratio in H-ZSM-5

Catalytic dehydration of methanol to dimethyl ether over micro–mesoporous ZSM-5/MCM-41 composite molecular sieves

Hierarchical Mesoporous ZSM-5 for the Dehydration of Methanol to Dimethyl Ether

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Catalytic Performances of Binder-free ZSM-5 Catalysts for Dehydration of Crude Methanol to Dimethyl Ether

Stability of Zeolite HZSM-5 in Liquid Phase Dehydration of Methanol to Dimethyl Ether

Catalytic oxidation of isoamyl alcohol on modified ZSM-5 molecular sieve catalysts prepared by different methods

Methane Dehydro-aromatization over Mo/HZSM-5 in the Absence of Oxygen: A Multinuclear Solid-State NMR Study of the Interaction between Supported Mo Species and HZSM-5 Zeolite with Different Crystal Sizes

Surface acidity and the dehydration of methanol to dimethyl ether

Cr/ZSM-5 for Ethane Dehydrogenation: Enhanced Catalytic Activity Through Surface Silanol

Regulation of Pore Structure and Acidity of a ZSM-5 Catalyst for Dehydration of Glycerol to Acrolein

Acidity, Crystallite Size and Pore Structure as Key Factors Influencing 1,3,5-Trimethylbenzene Hydrodealkylation Performance of NiMoS/ZSM-5

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Highly dispersed Ag2O-CuO nanospheres supported on γ-χ-Al2O3 for methanol dehydration to dimethyl ether

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Facile Synthesis of a Novel Hierarchical ZSM‐5 Zeolite: A Stable Acid Catalyst for Dehydrating Glycerol to Acrolein

Aluminum Fluoride Modified HZSM-5 Zeolite with Superior Performance in Synthesis of Dimethyl Ether from Methanol