PREPARATION OF AMORPHOUS AlO TEMPLATE

杨绍光,朱浩,洪建明,金志强,唐少龙,张世远

DOI: https://doi.org/10.3321/j.issn:0469-5097.2000.04.008

2000-01-01

Abstract:Porous alumina membranes with different pore diameters are prepared electrochemically. In the experiments, aluminum foil (99.5% purity) is used as the starting material. After annealed at 500℃ for 5 hours in the air, the aluminum foil is chemically polished in 1 M NaOH solution for 10 min. The membrane is carried out at a constant voltage in 0.3 mol/L sulphuric acid (HSO) for 4 hours. A mixture of ice and water provide a surrounding condition of 0℃. The remaining aluminum is removed in a saturated HgCI solution. 5 wt% phosphoric acid is used in the etching treatment step to get different pore diameters by changing etching time at 30℃. TEM images show that the diameter distribution of the pores is very narrow, and the pores are locally ordered. The pore diameter can he adjusted by changing the etching treatment time in a phosphoric acid solution. XRD illustrates that the porous membrane is in the amorphous state.