Preparation and Characterization of Porous Alumina Ceramic Membrane Support

Chen Ju-hon

Abstract:By adding pore forming agent and adhesive, the porous alumina ceramic membrane support were prepared by dry pressing and high temperature sintering with alumina powder of average size of 0.5 μm. During preparation, the orthogonal experiment was carried out to investigate the influences of sintering temperature, the amount of the adhesive, moulding pressure and the polyvinyl alcohol(PVA) concentration on the pure water flux of the membrane support, and to determine the optimal preparation conditions The microstructure of support was observed by SEM and the separation performance of membrane was tested by polyethylene glycol(PEG) retention. experiment. The results demonstrated that the pure water flux was significantly affected by the sintering temperature and the content of the adhesive, but little affected by the moulding pressure and the PVA concentration. The water flux reached 60 kg/(m2 h) and the molecular weight cut-off(MWCO) was 8500 when the adding amount of the adhesive was 1.75 w%, 80 mg/ml PVA solution was 2ml, the molding pressure was 9 MPa and sintering temperature was 1535 ℃.

Engineering,Materials Science