Preparation of Ultra-high Permeability Dual-layer Al 2 O 3 Hollow Fiber Supports for Zeolite Membrane Fabrication
Lin Huang,Ao Guo,Zhanzhao Yang,Jinyun Liu,Li Peng,Xuehong Gu
DOI: https://doi.org/10.1016/j.memsci.2024.123221
IF: 9.5
2024-08-19
Journal of Membrane Science
Abstract:Four-channel dual-layer Al 2 O 3 hollow fiber with ultra-high permeability and mechanical strength was prepared by co-extrusion and co-sintering technique for the first time and used as support for NaA zeolite membranes fabrication. The macroporous inner layer of the Al 2 O 3 hollow fiber, composed by large Al 2 O 3 particle, gives supports the high permeability and mechanical strength, while the thin out layer, composed by small particles, provides an even and smooth surface for zeolite membrane growth. By using SiO 2 as the sintering aid, the sintering temperature of the inner layer was reduced and match with that of the outer layer. The effects of SiO 2 adding amount, sintering temperature, Al 2 O 3 particle size and their content on the structure and properties of the prepared hollow fiber were investigated systematically. At a sintering temperature of 1520 °C, a dual-layer hollow fiber with surface pore size of 0.38 μm and fracture load of 24.52 N, exhibits pure water flux as high as 22.23 m 3 ·m -2 ·h -1 ·bar -1 . The NaA membrane prepared on this support achieved a flux of 14.14 kg·m -2 ·h -1 and a separation factor > 10000 in pervaporation separation of EtOH/H 2 O solution (90 wt.%, 75 °C). This work provides an efficient and low-cost way to prepare ceramic hollow fiber support for high-performance zeolite membrane fabrication.
engineering, chemical,polymer science