Abstract:Mordenite composite membranes were prepared by means of coating a porous α-alumina support with nanosized mordenite seeds followed by hydrothermal crystallization. A systematic investigation was performed on the influence of several factors such as ageing of the reaction mixture, alkalinity, salt addition and temperature on the formation of a mordenite membrane on the seeded support. The ageing of the reaction mixture reduces the growth rate of mordenite crystal along a-axis and b-axis but hardly influences the growth rate along c-axis. As a result, the boundaries between the surface crystals become a little larger with prolonging the period of ageing time. The growth rate of the mordenite crystal along individual axes increases first and then decreases with increasing concentration of sodium hydroxide. A higher alkalinity is unfavorable for the formation of a continuous mordenite membrane. The addition of salt in the reaction mixture has different effect on the growth rate of the mordenite crystal along each axis. With increasing the amount of salt, there was hardly influence on the growth rate along c-axis, whereas an obvious decline was observed in the growth rate along either a-axis or b-axis, which enlarges the boundaries between the surface crystals. The growth rate of the mordenite crystal increases more along c-axis than that along a-axis or b-axis with increasing temperature for hydrothermal crystallization. The use of a temperature as high as 473 K produces a membrane composed of bar-like crystals with larger boundaries.

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

High-performance zeolite membranes on inexpensive large-pore supports: highly reproducible synthesis using a seed paste.

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Preparation of Mordenite Composite Membranes with Seeding

ZSM-5 zeolite membranes prepared from a clear template-free solution

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Zeolite NaA membranes supported on alumina hollow fibers: Effect of support resistances on pervaporation performance

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

High-Performance Zeolite Naa Membranes on Polymer-Zeolite Composite Hollow Fiber Supports

High Performance Zeolite Lta Pervaporation Membranes on Ceramic Hollow Fibers by Dipcoating-Wiping Seed Deposition

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Zeolite Mfi Membranes for Separation of Ethanol/Water Mixture

The influence of nanoseeds on the pervaporation performance of MFI-type zeolite membranes on hollow fibers

Zeolite membranes on hollow fiber supports

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.