Abstract:Polycrystalline zeolite MFI (silicalite-1) membranes are successfully prepared by the secondary growth method on the α-Al2O3 hollow fibers with a high surface/volume ratio. Influences of the seed suspension concentration, the crystallization time and the content of the structure-directing agent (SDA, e.g., TPAOH) in the synthesis solution are investigated. As-synthesized zeolite seeds and membranes are characterized by X-ray diffraction (XRD), dynamic light scattering (DLS) and scanning electron microscopy (SEM) with energy dispersive X-ray (EDX). The membrane formation and integrity are found to be sensitively depending on the SDA contents in the synthesis solution and the seed amount of the seeded layer. High TPAOH content may cause aluminum leaching from the alumina support seriously and low TPAOH content may lead to non-continuous zeolite layer, leading to poor separation performance. A continuous and dense zeolite seed layer is necessary to obtain the silicalite-1 membrane with good quality. However, too thick seed layer may cause peeling and cracking of the membrane and thus decrease the separation performance. Appropriate TPAOH and seed amount may prevent the α-Al2O3 support leaching effectively. The silicalite-1 membranes prepared in this paper show the highest flux and relatively high separation factor of ethanol/water mixtures compared with the literature data.

The influence of nanoseeds on the pervaporation performance of MFI-type zeolite membranes on hollow fibers

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Influences of Seeds on the Properties of Zeolite NaA Membranes on Alumina Hollow Fibers

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Effects of Sodium Ions on the Separation Performance of Pure-Silica MFI Zeolite Membranes

Research Progress of Separation Mechanism and the Affecting Factors of Pervaporation Through Zeolite Membrane

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Manipulation of the Surface Microstructure and Its Effects on the Flux of NaA Zeolite Membranes in Pervaporation

Zeolite Mfi Membranes for Separation of Ethanol/Water Mixture

Zeolite NaA membranes supported on alumina hollow fibers: Effect of support resistances on pervaporation performance

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Fabrication of Zeolite Naa Membranes on Hollow Fibers Using Nano-Sized Seeds Exfoliated from Mesoporous Zeolite Crystals

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Influences of adding organic intermediate layer on membrane formation and properties

High Performance Zeolite Lta Pervaporation Membranes on Ceramic Hollow Fibers by Dipcoating-Wiping Seed Deposition

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Seeding-free Synthesis of High-Performance MFI Zeolite Membranes on Superhydrophobic Supports Inspired by “like Grows Like” Principle

Preparation and Characterization of High Performance MFI Zeolite Membrane in Ultradilute Solution

Nanocomposite Mfi-Alumina Hollow Fibre Membranes Prepared Via Pore-Plugging Synthesis: Influence of the Porous Structure of Hollow Fibres on the Gas/Vapour Separation Performance

Transfer Printing Platelike MFI Crystals As Seeds for the Preparation of Silicalite-1 Membranes