Effects of Per-Pass Reduction and Annealing Treatment on Microstructures and Mechanical Properties of Mg-Zn-Ce-Zr Alloy

张亚萍,靳丽,董杰,章桢彦,王瑶
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2012.11.001
2012-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The microstructures and mechanical properties of rolled Mg-0.5%Zn-0.5%Ce-0.5%Zr alloy were investigated. The alloy was rolled with different per-pass reductions (20%, 30%, 50%) at 400 ℃ and run speed of 10 m/min. The microstructures were observed by OM, SEM, TEM and XRD. The results show that only dynamic recovery (DRV) takes place in Mg-Zn-Ce-Zr alloy during rolling at 400 ℃ with various per-pass reductions. Meanwhile, more dislocations are found in 50% per-pass reduction rolled alloy. The overall texture intensity of {0001} basal plane is weaker for 20%per-pass reduction rolled alloys compared to 30% or 50%. After annealing at 500 ℃, the static recrystallization occurs in Mg-Zn-Ce-Zr alloy sheets. Texture weakening also happens after annealing, this is attributed to grain rotation during static recrystallization. Obvious anisotropy is found in the rolled alloys due to the basal texture, and then the anisotropy is weakened by texture randomization.
What problem does this paper attempt to address?