Abstract:Cordierite honeycomb ceramics are sintered under a range of sintering atmosphere and temperature conditions. The linear thermal expansion coefficient (CTE) is measured along the extrusion direction. The samples sintered in an enclosed crucible have a much lower CTE than those sintered in open air. The CTE decreases with increasing sintering temperature up to 1450 °C. The polymorphic phases, texture, amorphous phase, impurity crystals, and porosity are analyzed using scanning electron microscopy, HR‐TEM, porosimeter, and Rietveld refinement method. The sintered samples consist of two polymorphic phases: indialite (hexagonal symmetry) and cordierite (orthorhombic symmetry). Both the volume % of the cordierite phase and the crystal texture increase with increasing sintering temperature. The orthorhombic distortion of cordierite from the hexagonal lattice (indialite) increases with increasing sintering temperature. The characteristic six‐membered ring of the (Si,Al)‐O4 tetrahedra in the cordierite structure shows substantial changes in the bond length due to Al‐Si ordering. Amorphous phase and impurity crystal phases such as silimanite and spinel remain at temperatures as high as 1450 °C. The effect of the polymorphic phases, the degree of texture, amorphous phase, impurity crystal phases, and the orthorhombic distortion is discussed in relation to the CTE characteristics of honeycomb. The sintered honeycomb consists of two polymorphic phases, indialite (hexagonal symmetry) and cordierite (orthorhombic symmetry). The volume % of cordierite phase and the crystal texture increase with increasing sintering temperature. The thermal expansion coefficient (CTE) reduces with the sintering temperature. The orthorhombic distortion originates from Al‐Si ordering. Amorphous and silimanite phases are ascribed to higher CTEs of the samples sintered in open air.

WAYS TO DECREASE THE THERMAL EXPANSION COFFICIENT OF CORDIERITE USED IN HONEYCOMB CERAMICS

Synthesis of Cordierite with Low Thermal Expansion Coefficient

STUDY ON SUPPORT PROPERTIES OF POROUS CORDIERITE HONEYCOMB CERAMICS

A simple method for the preparation of cordierite ceramics with high strength and low thermal expansion coefficient

Crystal Structure and Thermal Expansion Coefficient of Cordierite Honeycomb Ceramics

Direct ink writing of cordierite ceramics with low thermal expansion coefficient

Direct Ink Writing of Porous Cordierite Honeycomb Ceramic

Fabrication of textured cordierite ceramics with low thermal expansion coefficient and custom structure via vat photopolymerization

Cordierite Honeycomb Ceramics Used for Purification of Vehicle Exhaust

Low-temperature preparation of porous cordierite-mullite ceramics using rice husk as silica source and pore-forming agent

Method for adjusting firing shrinkage of cordierite honeycomb ceramics by using amorphous silicon micropowder

Study on the Preparation of Flake Cordierite Powder

The Influence of Li+ on the Sintering of Cordierite Glass Ceramic

Effect of starch pore formers with different particle sizes on cordierite porous ceramics

The Inlfuence of Water Content on the Property and Structure of SiC Honeycomb Ceramic by Extrusion Molding Technology

Effect of Reduced Al2O3 Mole Ratio on Fabrication of Cordierite Ceramic by Solid-State Sintering Method

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

Preparation and Properties of Filtering Ceramics for High Temperature Exhaust Gas

The Influence of Li<sup>+</sup> on the Sintering of Cordierite Glass Ceramic

The study on fabrication of dielectric materials for low temperature Co-fired ceramics

Synthesis of Porous Cordierite Using Rice Husk As Silica Source and Pore Forming Agent