Mechanical Properties and Structure of Poly(p-phenylenevinylene) Films Prepared by the Zone-Reaction Method

H Okuzaki,N Ikeda,I Kubota,T Kunugi

DOI: https://doi.org/10.1021/ma9817875

IF: 5.5

1999-01-01

Macromolecules

Abstract:The “zone-reaction method”, consisting of zone drawing (ZD) and zone reaction (ZR), was applied to chemically synthesized poly(p-phenylenevinylene) (PPV) precursor films under various applied tensions (σ) and heater temperatures (Th). The changes in the structure, tensile, and viscoelastic properties of the resulting films were investigated. It was found that orientation function (f) of the ZD films increased with draw ratio (DR), regardless of the Th and σ values, and attained 0.862 (DR = 9). ZR was subsequently performed on the ZD film. The molecular orientation and PPV content were strongly affected by the Th:  The film obtained at Th = 240 °C exhibited the highest f value, as high as 0.894, while a further increase in the Th resulted in a disorientation of molecular chains. On the other hand, the absorption ratio between 632 cm-1 (C−S stretch) and 965 cm-1 (trans-vinylene C−H out-of-plane bend) (A632/A965) became almost zero at Th above 240 °C. The Young's modulus and tensile strength for the resultin...