Preparation of High‐modulus and High‐strength Poly(ethylene Terephthalate) Film by Zone‐annealing Method

T KUNUGI,C ICHINOSE,A SUZUKI

DOI: https://doi.org/10.1002/app.1986.070310211

IF: 3

1986-01-01

Journal of Applied Polymer Science

Abstract:AbstractThe zone‐annealing method was attempted to prepare high‐modulus and high‐strength poly(ethylene terephthalate) (PET) film. The film having Young′s modulus of 14.5 × 1010 dyn/cm2 and a tensile strength of 86.9 kg/mm2 in the drawing direction was obtained. These values correspond to four times those of a biaxial‐stretched PET film available commercially. The dyanmic viscoelastic properties also were measured. The dynamic storage modulus was 15.4 × 1010 dyn/cm2 at room temperature, and a high value of 3.6 × 1010 dyn/cm2 even at 200°C. The latter value is slightly higher than the room temperature modulus of the commercially available film. From the intensity and temperature position of α‐dispersion E″ peak, it was suggested that the amorphous chains in the zone‐annealed film was densely packed in a highly oriented state. Furthermore, the crystallinity, orientation, especially double orientation, and molecular chain conformation of the films in the zone‐annealing process are discussed in the present paper.