Abstract:The melt spinning process is the most common process to produce poly(ethylene terephthalate) (PET) fibers for textile and technical applications. The process involves extruding molten polymer through a spinneret followed by a drawing process. In the conventional drawing process, there appears to be an upper limit for draw ratio somewhere in the range of 3–9. Overcoming this limitation, superdrawing-based process offers a route to produce very fine denier fibers economically from as-spun fibers of 'normal' textile deniers, and it offers a unique method for quick-response manufacturing of fibers with various finer diameters (deniers) from a single spun supply. During superdrawing, PET fibers undergo large extension without significant crystallization or increase in molecular orientation. This study is directed at understanding the limitations of processing conditions for PET superdrawing process with temperatures ranging from 90 °C to 120 °C and strain rates from 0.008 s −1 to 0.425 s −1 . Evolution of crystallinity and molecular orientation of the drawn samples are evaluated using differential scanning calorimetry (DSC) and birefringence measurements. The results indicate that superdrawing is not possible for any strain rate at or below 90 °C because of significant strain-induced crystallization. Between 90 °C and 105 °C, superdrawing occurs only when the strain rate is below a threshold value, which increases from less than 0.333 s −1 to below 0.425 s −1 as temperature increases from 105 °C to 110 °C. Results also show that between 115 °C and 120 °C, superdrawing is only possible at strain rates higher than 0.016 s −1 . Increasing temperature from 110 °C to 120 °C leads to more crystallization at low strain rates (0.001 s −1 ), and less crystallization at high strain rates (0.1 s −1 ). The change of strain rate limitation from an upper bound to a lower bound around 110 °C for superdrawing suggests a change in molecular deformation mechanism based on a combination of factors such as the temperature, entanglement dynamics, and strain rate. The study also shows that the mechanism of crystallinity development in PET undergoes a transition at drawing temperature near 113 °C and strain rate of 0.17 s −1 .

Preparation of High-Modulus and High-Strength Poly(Ethylene-Terephthalate) Fiber by Zone Annealing

Preparation of High‐modulus and High‐strength Poly(ethylene Terephthalate) Film by Zone‐annealing Method

Preparation of High Modulus and High Strength Fiber by Zone-annealing Method

Preparation of High-Modulus Nylon-6 Fibre by an Improved Zone-Annealing Method

Preparation of Ultra-High Modulus Polyethylene Films by the Zone-Annealing Method

Drawing and Ultimate Tensile Properties of Modified Polyamide 6 Fibers

Preparation of High-Modulus Poly(ethylene Terephthalate) Fibers by Vibrating Hot Drawing

Application of Annealing under Extremely High Tension to Nylon 6 Fibers.

Optimizing Physical Aging in Poly(ethylene Terephthalate)-Glycol (PETG)

Application of a High-Tension Annealing Method to Nylon 66 Fibres

Combined Processing of Polypropylene Film by Coextrusion and Zone‐annealing

Microstructure and Mechanical Properties of Hot-Air Drawn Poly(ethylene-2,6-naphthalate) Fibers

Anisotropy of Dynamic Viscoelasticity for Uniaxially Drawn Poly(Ethylene-Terephthalate) Films and Its Temperature-Dependence

Preparation and Crystalline Properties of PET/ZnO Nano-meter Composite

Effect of strain rate and temperature on the crystallization behavior of amorphous poly(ethylene terephthalate) fibers during superdrawing

Effect of drawing and heat‐setting process on aggregate structure of Poly(ethylene terephthalate) industrial fiber in large‐scale spinning production

Bio‐based poly(trimethylene terephthalate)/polyamide 56 blend fibers via melt spinning: Preparation, structure, and properties

Two‐stage annealing method for short carbon fiber‐reinforced nylon 6 in fused filament fabrication

Large-scale control of morphology and tensile strength enhancement of PEEK fibers after post-treatment

Influences of isothermal annealing post‐treatment on mechanical performances in fused deposition modeling manufactured short carbon fibrous PETG and PA composites

The effects of UV aging process on the structure and properties of high-tenacity poly(ethylene terephthalate) industrial fiber