Abstract:A ZrB 2 -B 4 C functionally graded composite (FGM) tile with 100 mm diameter and 6 mm thickness with ZrB 2 content varying from 70% in the top layer to 10% in the bottom layer was fabricated using vacuum hot pressing. The density of the fabricated FGM is ~ 35% lower than monolithic ZrB 2 . To the best of our knowledge, ultra high temperature ceramic FGMs of such large dimensions have never been reported in the published literature. The FGM showed a smooth compositional transition without defects in the interlayer regions. Young's modulus of the FGM and its individual layers was determined using non-destructive ultrasound phase spectroscopy and overall Young's modulus of the FGM was correlated to the volume fraction averaged weighted sum of Young's modulus of each layer. The good interparticle bonding and lack of residual porosity in the top and middle layers resulted in high hardness and excellent wear resistance. The flexural strength of the FGM is approx. 400 MPa and the fracture mode displays a transition with composition along the thickness direction. Even under flexural loading, the interlayer regions remain intact, rendering excellent structural stability to the FGM. The fracture mechanism of the FGM has been discussed in light of the processing-induced thermal residual stress present in each layer and the presence of residual porosity and compositional gradient. The combination of low density, smooth interlayer transition, high flexural strength, as well as excellent hardness and wear resistance at the top layer renders the developed FGM potentially very attractive for thermal protection applications in hypersonic aircraft and re-entry vehicles.

A Novel Development of Zrb2/Zro2 Functionally Graded Ceramics for Ultrahigh-Temperature Application

Enhanced Mechanical Properties and Oxidation Resistance of Zirconium Diboride Ceramics via Grain‐Refining and Dislocation Regulation

A novel functionally graded material in the ZrB2–SiC and ZrO2 system by spark plasma sintering

Mechanical properties and fracture behavior of ultrahigh temperature ceramics at ultrahigh temperatures

Effect of graded microstructure on the modulus, hardness, and strength of hot-pressed ZrB2-B4C FGM

Research and Development of ZrB2-based Ultra-high Temperature Ceramics

ZrB2 and ZrB2–based Ceramics

Integrated preparation and enhanced performance of high-melting-point ZrC–Mo multilayer graded materials

Design and Preparation of an Ultra-High Temperature Ceramic by In-Situ Introduction of Zr2[Al(Si)]4C5 into ZrB2-SiC: Investigation on the Mechanical Properties and Oxidation Behavior

Ablation resistance behavior of ZrB2-SiC ultra-high temperature ceramics with Y2O3 addition

Processing and characterization of ZrB2–SiCW ultra-high temperature ceramics

Study on the ZrB2-SiCw Ultrahigh Temperature Ceramics

Oxidation Behaviors of ZrB2 Based Ultra-High Temperature Ceramics under Compressive Stress

Microstructure and Mechanical Properties of Zrb2-Based Uhtc Via Reactive Hot Pressing

High-temperature Oxidation Behavior of Monolithic Zr3[Al(Si)]4C6 and Its Composite Incorporating 30vol% ZrB2-SiC: Providing a Basis for Broadening the Service Temperature

Microstructure, mechanical properties, and reinforcement mechanism of carbide toughened ZrC-based ultra-high temperature ceramics: A review

Thermal shock behavior of ZrB2–SiC ultra-high temperature ceramics with addition of zirconia

Microstructure and high temperature mechanical properties of hot-pressed ZrB2-based composites

Preparation And Properties Of Dense Zrb2 Composite Reinforced By Elongated Sic And Al3bc3 Grains

Microstructural Evolution and Performance of Carbon Fiber-Toughened ZrB2 Ceramics with SiC or ZrSi2 Additive

Microstructure and mechanical properties of ZrB2–SiC–ZrO2f ceramic