Abstract:Erbium-doped silica glasses were made by sol-gel process. Intensive photoluminescence (PL) spectra from the Er-doped silica glasses at room temperature were measured. A broadband peak at 1535 ma, corresponding to the I-4(13/2)-I-4(15/2) transition, its full width at half-maximum (FWHM) of 10 nm, and a shoulder at 1546 nm in the PL spectra were observed. At lower temperatures, main line of 1535 nm and another line of 1552 Mn instead of 1546 nm appear. So two types of luminescence centers must exist in the samples at different temperature. The intensity of main line does not decrease obviously with increasing temperature. By varying the Er ion concentration in the range of 0.2 wt% - 5wt%, the highest photoluminescence intensity was obtained at 0.2wt% erbium doped concentration. Luminescence intensity decreases with increasing erbium concentration. Cooperative upconversion was used to explain the concentration quenching of luminescence from silica glass with high erbium concentration. Extended X-ray absorption fine structure measurements were carried out. It was found that the majority of the erbium impurities in the glasses have a local structure of eight first neighbor oxygen atoms at a mean distance of 0.255 nm, which is consistent with the typical coordination structure of rare earth ion.

Highly Efficient Emission of Er3+ in a Functionalized Mesoporous Silica

Efficient Sensitized Photoluminescence from Erbium Chloride Silicate Via Interparticle Energy Transfer

Sensitizing Properties of Luminescence Centers on the Emission of Er3+ in Si-Rich Sio2 Film

Luminescent Character of Mesoporous Silica with Er2o3 Composite Materials

Control of the Formation and Luminescent Properties of Polymorphic Erbium Silicates on Silicon

Sensitized Photoluminescence of Erbium Silicate Synthesized on Porous Silicon Framework

Highly efficient near-infrared emission in Er3+ doped silica films containing size-tunable SnO2 nanocrystals.

Enhancement of Sensitized Photoluminescence of Erbium Chloride Silicate Through Regulating Annealing

Correlation Of Efficient Luminescence With Crystal Structures Of Y-Er2si2o7 And Alpha-Er2si2o7 In Er-Doped Silicon Oxide Films

Enhanced Luminescence of Erbium Silicate: Interstitial Lithium Directly Regulates the Lattice Structure of Erbium Compound Crystals

Efficient Sensitized Photoluminescence of Er Silicate in Silicon Oxide Films Embedded with Amorphous Silicon Clusters, Part I: Fabrication

Enhanced Luminescence of Erbium Doped Ga2O3 Films and Devices by Optimizing Annealing Process

Optical Absorption and Emission Properties of Er3+ Doped Mixed Alkali Borosilicate Glasses

Preparation And Characterization Of Erbium Doped Sol-Gel Silica Glasses

Up-conversion luminescence and near infrared luminescence of Er3+ in transparent oxyfluoride glass-ceramics

Strong Energy-Transfer-Induced Enhancement of Er3+ Luminescence in In2o3 Nanocrystal Codoped Silica Films

Preparation and Spectroscopic Properties of Er3+-doped High Silica Glass Fabricated by Sintering Nanoporous Glass

Boosting Near-Infrared Photoluminescence Efficiency of Erbium Ions and ZnO Quantum Dots Codoped Amorphous Silica Thin Films

Spectral properties of Er3+ doped high silica glass

Efficient 2 Μm Emission in Er3+/Ho3+ Co-Doped Lead Silicate Glasses under Different Excitations

1.53νm photo-and electroluminescence from Er3+ in erbium silicate