Spectroscopic Investigations of Nd3+-, Er3+-, Er3+/Yb3+-, and Tm3+-ions Doped SiO2–Al2O3–CaF2–GdF3 Glasses
G. Lakshminarayana,Mengfei Mao,Rong Yang,J. R. Qiu,M. G. Brik
DOI: https://doi.org/10.1016/j.physb.2009.05.042
IF: 2.988
2009-01-01
Physica B Condensed Matter
Abstract:This paper reports on the absorption, visible and near-infrared luminescence properties of Nd3+, Er3+, Er3+/2Yb3+, and Tm3+ doped oxyfluoride aluminosilicate glasses. From the measured absorption spectra, Judd–Ofelt (J–O) intensity parameters (Ω2, Ω4 and Ω6) have been calculated for all the studied ions. Decay lifetime curves were measured for the visible emissions of Er3+ (558nm, green), and Tm3+ (650 and 795nm), respectively. The near infrared emission spectrum of Nd3+ doped glass has shown full width at half maximum (FWHM) around 45nm (for the 4F3/2→4I9/2 transition), 45nm (for the 4F3/2→4I11/2 transition), and 60nm (for the 4F3/2→4I13/2 transition), respectively, with 800nm laser diode (LD) excitation. For Er3+, and Er3+/2Yb3+ co-doped glasses, the characteristic near infrared emission bands were spectrally centered at 1532 and 1544nm, respectively, with 980nm laser diode excitation, exhibiting full width at half maximum around 50 and 90nm for the erbium 4I13/2→4I15/2 transition. The measured maximum decay times of 4I13/2→4I15/2 transition (at wavelength 1532 and 1544nm) are about 5.280 and 5.719ms for 1Er3+ and 1Er3+/2Yb3+ (mol%) co-doped glasses, respectively. The maximum stimulated emission cross sections for 4I13/2→4I15/2 transition of Er3+ and Er3+/Yb3+ are 10.81×10−21 and 5.723×10–21cm2. These glasses with better thermal stability, bright visible emissions and broad near-infrared emissions should have potential applications in broadly tunable laser sources, interesting optical luminescent materials and broadband optical amplification at low-loss telecommunication windows.