Abstract:The multiphase material developed through self‐assembly engineering exhibits a high oxygen vacancy concentration. This consequently enhances its proton defect formation and transport with a low enthalpy of protonation reaching −30 ± 9 kJ mol−1. The peak power density of the single cell reaches 1054 mW cm−2 at 650 °C with good operation stability spanning over 500 h at 550 °C. Triple ionic and electronic conductivity (TIEC) in cathode materials for protonic ceramic fuel cells (PCFCs) is a desirable feature that enhances the spatial expansion of active reaction sites for electrochemical oxygen reduction reaction. The realization of optimal TIEC in single‐phase materials, however, is challenging. A facile route that facilitates the optimization of TIEC in PCFC cathodes is the strategic development of multiphase cathode materials. In this study, a cubic‐rhombohedral TIEC nanocomposite material with the composition Ba(CeCo)0.4(FeZr)0.1O3−δ (BCCFZ) is designed via self‐assembly engineering. The material consists of a mixed ionic and electronic conducting phase, BaCo1−(x+y+z)CexFeyZrzO3−δ (M‐BCCFZ), and a dominant proton‐conducting phase, BaCe1−(x+y+z)CoxZryFezO3−δ (H‐BCCZF). The dominant cerium‐rich H‐BCCFZ phase enhances the material's oxygen vacancy concentration and the proton defects formation and transport with a low enthalpy of protonation of −30 ± 9 kJ mol−1. The area‐specific resistance of the BCCFZ symmetrical cell is 0.089 Ω cm2 at 650 °C in 2.5% H2O‐air. The peak power density of the anode‐supported single cell based on BCCFZ cathode reaches 1054 mW cm−2 at 650 °C with good operation stability spanning over 500 h at 550 °C. These promote BCCFZ as a befitting cathode material geared toward PCFC commercialization.

High Performance Low Temperature Ceramic Fuel Cell with Zinc Doped Ceria-Carbonates Composite Electrolyte

Stable, easily sintered BaCe0.5Zr0.3Y0.16Zn0.04O3−δ electrolyte-based protonic ceramic membrane fuel cells with Ba0.5Sr0.5Zn0.2Fe0.8O3−δ perovskite cathode

A high performance intermediate temperature fuel cell based on a thick oxide–carbonate electrolyte

Novel Intermediate Temperature Ceramic Fuel Cells with Doped Ceria-Based Composite Electrolytes

Introducing Catalyst in Alkaline Membrane for Improved Performance Direct Borohydride Fuel Cells

Ceramic fuel cells using novel proton-conducting BaCe0.5Zr0.3Y0.1Yb0.05Zn0.05O3-δ electrolyte

Novel Doped Barium Cerate–carbonate Composite Electrolyte Material for Low Temperature Solid Oxide Fuel Cells

A high-performance ceramic fuel cell with samarium doped ceria–carbonate composite electrolyte at low temperatures

Doped ceria–chloride composite electrolyte for intermediate temperature ceramic membrane fuel cells

Intermediate temperature fuel cell with a doped ceria–carbonate composite electrolyte

Intermediate-to-low temperature protonic ceramic membrane fuel cells with Ba0.5Sr0.5Co0.8Fe0.2O3-δ–BaZr0.1Ce0.7Y0.2O3-δ composite cathode

Performance of fuel cells with proton-conducting ceria-based composite electrolyte and nickel-based electrodes

Analyzing the composite heterostructure as an efficient electrolyte for low-temperature ceramic fuel cells

Improved Ionic Transport Using a Novel Semiconductor Co0.6Mn0.4Fe0.4Al1.6O4 and Its Heterostructure with Zinc Oxide for Electrolyte Membrane in LT-CFCs

Study on GDC-KZnAl Composite Electrolytes for Low-Temperature Solid Oxide Fuel Cells

Preparation and characterization of Ni-Fe-CCC composite for low-temperature ceramic fuel cell

Ceramic Fuel Cells Based on Ceria–carbonate Salt Composite Electrolyte

Electrochemical Performance and Enhancement of Hydration Kinetics on BaCo 0.7 Fe 0.2 Zr 0.1 O 3−δ Cathode for Protonic Ceramic Fuel Cells

NOVEL CERAMIC FUEL CELLS BASED ON CERIA-SALT COMPOSITE ELECTROLYTE

Electrokinetic Insights into the Triple Ionic and Electronic Conductivity of a Novel Nanocomposite Functional Material for Protonic Ceramic Fuel Cells

Analysis and Modeling of Novel Low-Temperature SOFC with a Co-Ionic Conducting Ceria-Based Composite Electrolyte