Co-precipitation process as an effective and viable route for proton-conducting solid oxide fuel cell applications
Liqiong Yang,Haoliang Tao,Junkang Sang,Qihang Ren,Qingfeng Teng,Guoxin Chen,Wanbing Guan,Yu Chen,Liangzhu Zhu
DOI: https://doi.org/10.1016/j.ijhydene.2024.04.201
IF: 7.2
2024-04-24
International Journal of Hydrogen Energy
Abstract:BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3-δ (BCZYYb) is one of the most popular electrolyte materials in proton ceramic fuel cells (PCFCs). The synthesizing method and properties of BCZYYb powders have a significant impact on the sintering activity of electrolyte materials. In this work, the BCZYYb electrolyte was synthesized by ammonium bicarbonate co-precipitation method (CPT), and was compared with the powder produced by solid-state reaction (SSR) and sol-gel (SG) methods. XRD results show the BCZYYb powder synthesized by the CPT method belongs to orthorhombic crystal system with a space group of Pmcn (No. 62) and the refined lattice parameters are a = 8.774 Å, b = 6.173 Å, and c = 6.203 Å. In humid air atmosphere, the total conductivity at 650 °C and the activation energy for the BCZYYb powder prepared via the CPT method was 2.1 × 10 −2 S cm −1 and 0.46 eV, respectively, as compared with 1.9 × 10 −2 S cm −1 and 0.45 eV for the SSR method, and 1.8 × 10 −2 S cm −1 and 0.44 eV for the SG method. Under similar testing conditions, the measured peak power densities were 0.51, 0.35, and 0.40 W cm −2 at 650 °C for the anode supported PCFCs using electrolyte powder prepared via CPT, SSR and SG methods, respectively, which proves the CPT method is an effective and viable route for PCFCs applications.
energy & fuels,electrochemistry,chemistry, physical