Formation of Al2O3–Bi4Ti3O12 nanocomposite oxide films on low-voltage etched aluminum foil by sol–gel processing

Xianfeng Du,Youlong Xu

DOI: https://doi.org/10.1016/j.surfcoat.2007.08.020

IF: 4.865

2008-01-01

Surface and Coatings Technology

Abstract:A water-based bismuth titanate Bi4Ti3O12 (BTO) sol was synthesized by mixing bismuth nitrate, tetra-n-butyl titanate, lactic acid, acetic acid and distilled water. The sol was applied to low-voltage etched aluminum foil by dip-coating. The crystallization process of Bi4Ti3O12 on low-voltage etched aluminum foil was measured by thermal gravimetry–differential scanning calorimetry (TG–DSC) and high-temperature X-ray diffraction (HT-XRD). It was found that Bi4Ti3O12 sol first converted into intermediate phase Bi1.74Ti2O6.624, then transformed into perovskite phase Bi4Ti3O12. After annealed at 600 °C for 30 min in air, the low-voltage etched aluminum foil covered with Bi4Ti3O12 sol was anodized galvanostatically in 15 wt.% ammonium adipate solution. The voltage–time variation during anodizing was monitored and recorded. The structure and composition of samples were investigated by field emission scanning electron microscopy (FE-SEM) and energy dispersive X-ray analysis (EDAX). Results showed that the anodic composite oxide film was composed of an inner Al2O3 layer and an outer Bi4Ti3O12 layer. The specific capacitance and the product of specific capacitance and withstanding voltage of samples with a BTO coating were about 56.64% and 43.77% larger than that without a BTO coating.