Effect of Nickel on the Properties of Vitrified Bond for Diamond Grinding Tool

Zhiqi WANG,Long WAN,Weida HU,Xiaopan LAU,Haochong ZHAI,Junsha WANG

DOI: https://doi.org/10.3969/j.issn.1005-023X.2012.04.022

2012-01-01

Abstract:The vitrified bond mixing with different amounts of Ni(Ni/VB) was prepared by the method of powder metallurgy.The microstructure,interfaces,oxidizability and the compressive strength of the Ni/VB were analyzed by SEM,EDS,XRD,TG-DSC and three-point bending test.The wettability between the different vitrified bonds and the diamonds was also investigated.The results showed that the adding Ni had little effect on the refractoriness and the liquidity of the vitrified bond,but reducing the firing shrinkage of the vitrified bond.The interface between the vitrified bond and the Ni was closely bonding at 750℃.With adding the content of 15wt%Ni,the compressive strength of the Ni/VB got the maximum,62.8MPa,which was higher 19.41% than the non-adding Ni.It was also found that the adding Ni could give a better wettability between the vitrified bond and the diamonds at high temperatures.The wetting angle between the Ni/VB and the diamonds was 64°,which was lower 24.3% that the non-adding Ni(84.5°).