Fabrication and performance evaluation of metal bond diamond tools based on aluminothermic reaction
Ming-cong Li,Feng-lin Zhang,Jia-hong Chen,Meng-jie Zhai,Mei-xing Zhu,Yu-mei Zhou,Feng Chen,Zhi-qiao Yan
DOI: https://doi.org/10.1016/j.ijrmhm.2020.105293
IF: 4.804
2020-11-01
International Journal of Refractory Metals and Hard Materials
Abstract:<p>Herein, the fabrication of metal bond diamond tools is proposed by using the Fe<sub>2</sub>O<sub>3</sub>-Al aluminothermic reaction. Moreover, the influence of sintering temperature and TiH<sub>2</sub>- and Si-doping on phase composition and mechanical properties of the reactive sintered bond is investigated. Furthermore, the grinding performance of metal bond diamond tool on ceramic tile is also examined. At 930 °C, the sintered bond is composed of Fe, Al<sub>2</sub>O<sub>3</sub>, Fe<sub>3</sub>O<sub>4</sub> and FeO phases. However, the aluminothermic reaction initiated at 1028.8 °C and resulted in the formation of FeAl<sub>2</sub>O<sub>4</sub> and Fe<sub>3</sub>Al phases. Moreover, the content of Al<sub>2</sub>O<sub>3</sub>, Fe<sub>3</sub>Al, <em>α</em>-Fe and FeAl<sub>2</sub>O<sub>4</sub> phases increased with the increase of sintering temperature. The maximum flexural strength, hardness and relative density are achieved when sintering at 1230 °C. In addition, the dehydrogenation of TiH<sub>2</sub> can impede the formation of FeAl<sub>2</sub>O<sub>4</sub> phases and improve the flexural strength, hardness and relative density of the bond. Also, the Si-doping into Fe<sub>2</sub>O<sub>3</sub>-Al aluminothermic reaction system resulted in Fe<sub>2</sub>Al<sub>3</sub>Si<sub>3</sub> phase and reduced the content of Al<sub>2</sub>O<sub>3</sub> and Fe<sub>3</sub>Al phases, leading to higher flexural strength, lower hardness and inferior relative density. In wet grinding, the as-prepared metal bond diamond tool can be used to grind ceramic tiles with lower grinding force and better surface quality than the dry grinding. However, the as-prepared metal bond diamond tool rendered low wear resistance due to the brittle nature of the metal bond.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering