Effect of Pretreatment Strategy on the Microstructure, Mechanical Properties and Cutting Performance of Diamond Coated Hardmetal Tools Using HFCVD Method
Shuyu Fan,Tongchun Kuang,Wei Xu,Yuming Zhang,Yifan Su,Songsheng Lin,Di Wang,Hongzhi Yang,Kesong Zhou,Mingjiang Dai,Lei Wang
DOI: https://doi.org/10.1016/j.ijrmhm.2021.105687
2021-01-01
Abstract:Diamond coatings are deposited on cemented carbide (WC-Co) tools to lengthen their cutting lifetime. However, their industrial application is held back by poor diamond coating-substrate adhesive strength. In this paper, the cutting performance of differently pretreated diamond-coated WC-Co tools for graphite milling was examined. The WC and Co phases on the surface of the WC-Co substrates were treated by a three-step acid-Murakami-acid chemical etching process (AMA-treatment) followed by physical vapor deposition (PVD) of a WC interlayer with a thickness of 250, 500, or 750 nm. Finally, a multilayered coating was obtained by depositing a 4 mu m thick diamond coating using hot filament chemical vapor deposition (HFCVD). The effect of this composite pretreatment on the adhesive strength and cutting performance of diamond-coated WC-Co tools were studied and compared with diamond-coated WC-Co tools only pretreated by either AMA-treatment or deposition of a 500 nm WC interlayer. Adhesive strength tests assessed by the Rockwell indentation method showed that a combination of AMA-treatment and a thinner WC interlayer (250 or 500 nm) enhanced the adhesive strength (HF1) and cutting performance of these diamond-coated WC-Co tools. SEM and EDS analyses indicated that coating delamination, fracture, diffusion, and adhesive wear were the main failure mechanisms of the cutting tools. Finally, in graphite cutting tests, the diamond-coated WC-Co tool with a composite pretreatment consisting of AMA-treatment and deposition of a 250 nm WC interlayer exhibited significantly enhanced cutting performance (VBmax = 0.18 mm at a cutting length of 200 m) compared with the other pretreated tools.