Abstract:This study analyzes the influence of different ultrasonic amplitudes on the microstructure composition, microhardness, tensile strength, and corrosion resistance of Al alloy/steel laser welding-brazing joints assisted by ultrasonic vibration. The application of ultrasonic vibration did not change the microstructure composition of the joints but refined them. The joints were all composed of θ-Fe(Al, Si)3 and τ5-Al7.2Fe1.8Si formed at the interface reaction zone, as well as an α-Al solid solution and Al-Si eutectic phase generated in the weld seam zone. Meanwhile, the thickness of the IMCs at the interface decreased with an increase in the ultrasonic amplitude. When the ultrasonic amplitude was 8 μm, the IMCs thickness was a minimum of 1.62 μm. In this condition, the reduction of the IMCs thickness and the refined grain of joints made the microhardness and tensile strength reach the maximum. The fracture of joints with ultrasonic amplitudes of 0 and 4.8 μm began at the weld seam and extended to the interface reaction zone at the steel side, while the fracture of joints was located in the heat-affected zone (HAZ) of the Al alloy side when the ultrasonic amplitude was 8.0 and 11.2 μm. The fracture mode of the former presented a typical mixed fracture with cleavage steps and tearing edges, and that of the latter showed ductile fracture with uniform and fine ductile dimples. The corrosion resistance of the joints was improved by adding ultrasonic vibration. When the ultrasonic amplitude was 8 μm, its corrosion resistance was optimum; it was ascribed to a dense oxide film formed on the surface of the metal under the action of ultrasonic vibration.

Impact of ultrasonic vibration on microstructure and mechanical properties of diamond in laser brazing with Ni–Cr filler alloy

Effect of ultrasonic on properties of electroplated diamond tools

Microstructure and properties at bonds of diamond grains and Ni Cr filler alloy by fiber laser brazing

Cu-induced enhancement of interfacial bonding for brazed diamond grits with NiCr filler alloys

A Novel Diamond/AlSi Composite Coating on Ti-6Al-4V SubStrate Made by Ultrasonic-Assisted Brazing

Effects of ultrasonic vibrations on brazing mechanism and evaluating grinding performance of CBN tools

Effects of Ce and La elements on interfacial bonding, thermal damage and mechanical performance of brazed diamonds with Ni Cr filler alloy

Microstructure and properties of brazed diamond with Pr-modified Ni Cr filler metals

Microstructure and mechanical properties of single-crystal diamond/Kovar alloy joints brazed with an AgCuTi metal filler

Effect of an Ultrasonic Vibration on the Microstructure and Properties of Al Alloy/Steel Laser Welding-Brazing Joints

Interfacial Structure of Diamond Brazing with Cu-Sn-Cr

Exploring the trace rare earth Sm on the microstructure and mechanical performance of brazed diamonds by Ni–Cr filler alloy

Effect of Nd element on the microstructure and mechanical performance of brazed diamonds with Ni–Cr filler metal

An Investigation on the Vacuum Brazed Diamond Film and Copper Using Low-Temperature Ag-Cu-Sn-Ti Filler Alloys: Interfacial Microstructure and Mechanical Performance

Microstructure and Processing Performance of Brazed Diamond Drill Bits with Ni–Cr + Cu–Ce Composite Solder

Microstructure and Mechanical Properties of Pre-Brazed Diamond Abrasive Grains Using Cu–Sn–Ti Alloy

Effect of Cu Ce Alloy Addition on the Microstructure and Mechanical Performance of Brazed Diamonds with Ni Cr Alloy

High Power CO2 Laser Brazing of Diamond Grits

Enhanced Machinability of Ni-based Single Crystal Superalloy by Vibration-Assisted Diamond Cutting

Interfacial microstructure and performance of nano-diamond film/Ti-6Al-4V joint brazed with AgCuTi alloy

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2