Effects of Heat Treatment on the Tensile Behavior and Damage Evolution of A 3d C/Sic Composite

Yiqiang Wang,Litong Zhang,Laifei Cheng
DOI: https://doi.org/10.1142/s0217979210065313
2010-01-01
Abstract:The tensile responses and the associated damage evolutions of a 3D C/SiC composite with and without heat treatment on the fiber preforms were compared. The results show that the composite without heat treatment exhibits a largely non-linear stress-strain behavior up to rupture as well as a lower strength and a strain-to-failure. The damage evolution characterized by acoustic emission indicates the composite failures in the region of matrix cracking multiplication. However, the composite with heat treatment has a larger strength and a strain-to-failure, and the damage evolution indicates that the composite had experienced the region of matrix cracking saturation and then fiber bundle pull-out just prior to final failure. Microstructural observations on the fractured specimens revealed the interfacial bonding between fibers and matrix becomes weaker after heat treatment.
What problem does this paper attempt to address?