Abstract:The CoFeCu coating was electrodeposited onto a silicon substrate from a sulfate solution containing organic additives (saccharin and sodium acetate). The effects of deposition time and metal ion concentration in the bath on the magnetic and microstructural properties were studied. The deposited films were characterized by scanning electron microscopy (SEM) coupled with energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), atomic force microscopy (AFM), and vibrating sample magnetometer (VSM) measurements. Composition analysis revealed that different ternary Co 72 Fe 15 Cu 13 , Co 81 Fe 10 Cu 9 , and Co 77 Fe 18 Cu 5 samples were obtained when the deposition times were varied. The SEM images of the CoFeCu samples exhibited a compact surface comprising finer grain agglomerates. The Co 77 Fe 18 Cu 5 samples plated at longer deposition times showed the formation of nano-voids compared to the Co 72 Fe 15 Cu 13 and Co 81 Fe 10 Cu 9 samples plated at shorter deposition times. In all samples, the fcc(Co) phase was dominant. From the magnetic analysis, good soft magnetic properties were obtained, with a coercivity of 6 Oe and a saturation magnetization of 1494 emu/cm 3 (1.87 T) for the Co81Fe10Cu9 sample. Increasing the concentration of cobalt ions and decreasing the concentrations of iron and copper ions in the electroplating solution improved the soft magnetic properties of the CoFeCu deposit. The composition of the CoFeCu deposit changed as the concentration of cobalt ions was increased in the electroplating solution. The Co 81 Fe 10 Cu 9 sample had a higher saturation magnetization (MS) of 2005 emu/cm 3 (2.5 T) and an acceptable lower coercivity of 19 Oe. This work successfully fabricated CoFeCu thin films with good soft magnetic properties on a Si substrate.

In-situ external reflection FTIR spectroelectrochemical and XPS investigations of cobalt-cyanometallates as inorganic polymeric materials on a platinum electrode

Preparation, characterization and application in cobalt ion adsorption using nanoparticle films of hybrid copper–nickel hexacyanoferrate

Preparation and Electrochemical Property of Copper Cobalt Hexacyanoferrate Hybrid Film

Synchrotron Radiation in Situ X-ray Absorption Fine Structure and in Situ X-ray Diffraction Analysis of a High-Performance Cobalt Catalyst Towards the Oxygen Reduction Reaction

Electrodeposition and characterization of nanocrystalline CoNiFe films

Electrochemical Behavior of Cobalt from 1-Butyl-3-methylimidazolium Tetrafluoroborate Ionic Liquid

Redox behavior of unsubstituted cobalt phthalocyanine in nanostructured Langmuir-Schaefer films

Synthesis, Characterization and Electrocatalytic Properties of FeCo Alloy Nanoparticles Supported on Carbon Nanotubes

Structural, Morphological, and Magnetic Properties of Electrodeposited CoNi Thin Films on the FTO Substrate

Surface-renewable Cobalt(ii) Hexacyanoferrate-Modified Graphite Organosilicate Electrode and Its Electrocatalytic Oxidation of Thiosulfate.

Electrodeposition of Nanocrystalline Conife Thin Films Prepared by Cyclic Voltammetry

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

Electrochemical Characterisation of Co@Co(OH) 2 Core‐Shell Nanoparticles and their Aggregation in Solution

Effect of cobalt content on electrodeposition and properties of Co–Ni alloy thin films

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Influence of deposition parameters on the electrodeposited ternary CoFeCu coatings

Altered electrochemistry of poly(3,4-ethylenedioxythiophene) after activation of the inserted cobalt ions

Deposition of Ni–Co by cyclic voltammetry method and its electrocatalytic properties for oxygen evolution reaction

Enrichment and activation of cyano in cobalt hexacyanoferrate for specific recovery of ultra-low concentrations of platinum

Potentiostatic electrodeposition of polyaniline-cobalt and its electrochemical properties

Characterization of the Magnetism and Structure of Metastable Co Films Grown by Electrochemical Epitaxy