Surface Modification of CaCO3 by Ultrasound-Assisted Titanate and Silane Coupling Agents

Peng Cheng,Lei Yang,Yuxiong Xie,Yu Liu

DOI: https://doi.org/10.3390/ma16103788

IF: 3.4

2023-05-18

Materials

Abstract:Calcium carbonate (CaCO3) is a widely used inorganic powder, but its industrial applications are limited by its hydrophilicity and oleophobicity. Surface modification of CaCO3 can improve its dispersion and stability in organic materials and further improve its potential value. In this study, CaCO3 particles were modified with silane coupling agent (KH550) and titanate coupling agent (HY311) combined with ultrasonication. The oil absorption value (OAV), activation degree (AG), and sedimentation volume (SV) were employed to evaluate the modification performance. The results showed that the modification effect of HY311 on CaCO3 was better than that of KH550, and ultrasonic treatment played an auxiliary role. Based on response surface analysis, the optimal modification conditions were determined as follows: the HY311 dosage was 0.7%, the KH550 dosage was 0.7%, and ultrasonic time was 10 min. The OAV, AG, and SV of modified CaCO3 under these conditions were 16.65 g DOP/100 g, 99.27%, and 0.65 mL/g, respectively. The SEM, FTIR, XRD and thermal gravimetric analyses indicated successful coating of HY311 and KH550 coupling agents on the surface of CaCO3. The optimization of the dosages of two coupling agents and ultrasonic time improved the modification performance significantly.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the issue of surface modification of calcium carbonate (CaCO₃) using titanate (HY311) and silane coupling agent (KH550) under ultrasonic assistance to improve its dispersibility and stability in organic materials. Specifically, the paper aims to:

1. Investigate the effects of KH550 and HY311, either alone or in combination with ultrasonic treatment, on the surface modification of CaCO₃.
2. Optimize the best conditions for KH550 and HY311 modification under ultrasonic assistance based on Response Surface Methodology (RSM).
3. Verify the performance of the modified CaCO₃ through characterization methods such as Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR), Thermogravimetric Analysis (TGA), and X-ray Diffraction (XRD).

The main goal of the paper is to improve the oleophilicity and hydrophobicity of CaCO₃ through these studies, thereby enhancing its potential in industrial applications, particularly in the dispersibility and compatibility within polymer matrices.