Magnetic properties and structure of short-term annealed FeCuBPSi nanocrystalline alloys

Beata Butvinová,Peter Švec Sr,Irena Gejdoš Janotová,Leonardo Viana Dias,Dušan Janičkovič,Igor Maťko

DOI: https://doi.org/10.1016/j.jmmm.2023.171662

IF: 3.097

2024-01-04

Journal of Magnetism and Magnetic Materials

Abstract:Alloys with composition Fe 80−x Cu 1 B 11 P 4 Si 4+x (x = 0 and 4), i. e. with Si 4 at % or 8 at % have been prepared by rapid quenching from the melt in air. For comparison the alloy with P 3 at % and Si 8 at % has been investigated as well. As-quenched structure of all ribbons was checked by X-ray diffraction. Subsequently the samples were submitted to thermal analysis, scanning and transmission electron microscopy and magnetic measurements. Hysteresis loops of strips after short-term annealing at 400, 420 and 500 °C for 5 min changed their shape – the saturation magnetic polarization increased. Its value changed from 1.67 to 1.74 T depending of the crystalline volume fraction for Fe 80 Cu 1 B 11 P 4 Si 4 alloy. Addition of Si to the studied P 4 at % alloy leads to a decrease of coercivity after short-term annealing at the temperatures below the onset of the first transformation. Magnetic work decreased several times and its orientation acquired the distinct orientation along the ribbon axis.

materials science, multidisciplinary,physics, condensed matter