Abstract:New Fe82-85B13-16Si1Cu1 amorphous alloys with low B content and high B/Si content ratios were synthesized by melt spinning for developing good soft magnetic and high strength materials. The crystallization occurs through two stages and the first-stage onset temperature increases from 673 K to 705 K with increasing B content, while the second-stage temperature remains nearly constant. The first and second stages are due to the precipitation of the α-Fe(Si) phase with a size of about 30 nm and the decomposition of the remaining amorphous phase to α-Fe(Si)+Fe3B+Fe2B, respectively. The Fe-based alloys exhibited good soft magnetic properties both in annealed amorphous and nanocrystallized amorphous+α-Fe(Si) phases. The saturated magnetic flux density, coercivity and permeability at 1 kHz are 1.7 T, 4.92 A/m and 7100, respectively, for the annealed amorphous 14B alloy and 1.74 T, 5.62 A/m and 10100, respectively, for the nanocrystallized 13B alloy. The Vickers hardness (H v) is 803–867 for the as-spun state and it increases with decreasing B content. The H v increases significantly by crystallization to α-Fe+amorphous phases and reaches 997–1550 for the alloys annealed at 693–763 K just before T x2. The ultrahigh H v is presumably due to the combination of fine nanoscale mixed phases, high volume fraction of α-Fe(Si) without internal defects and the enrichment of B into the remaining amorphous phase. Such ultrahigh H v has not been obtained for Fe-based amorphous and crystallized alloys before and the addition of 1%Cu is essential for the ultrahigh H v and the amorphous phase formation for the Fe-rich 85%Fe alloy. The new Fe-based alloys are encouraging as future soft magnetic and ultrahigh strength materials with low material cost.

Tunable and attractive magnetic properties of FeBPSiCu alloys

Improving the Amorphous Forming Ability and Magnetic Properties of FeSiBPCu Amorphous and Nanocrystalline Alloys by Utilizing Carbon

The Effects of Si Substitution with C on the Amorphous Forming Ability, Thermal Stability, and Magnetic Properties of an FeSiBPC Amorphous Alloy

Optimization of Crystallization Behavior and Soft Magnetic Properties of the Si-free Fe-B-P-C-Cu Nanocrystalline Alloys by Cu Content Tuning

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Investigation of glass forming ability, crystallization behavior, and soft magnetic properties of Fe–B–P–C–Cu alloy ribbons

Ultra-fine microstructure and exceptional low coercivity developed in a high-Bs Fe-Si-B-P alloy by co-alloying Ni, Mo, and Cu

Crystallization behavior, soft magnetic properties and good bending ductility of high Fe content FeSiBCuPC alloys induced by composition design

Local Structure, Nucleation Sites and Crystallization Behavior and Their Effects on Magnetic Properties of Fe81Si X B10P8−xCu1 (x = 0~8)

Fe-based nanocrystalline FeBCCu soft magnetic alloys with high magnetic flux density

Tailoring Soft Magnetic Properties of Fe-based Amorphous Alloys Through C Addition

The role of Cu content on structure and magnetic properties of Fe–Si–B–P–Cu nanocrystalline alloys

Nanocrystallization, good soft magnetic properties and ultrahigh mechanical strength for Fe82-85B13-16Si1Cu1 amorphous alloys

Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

Excellent Soft Magnetic Properties and Enhanced Glass Forming Ability of Fe-Si-B-C-Cu Nanocrystalline Alloys

Soft magnetic properties of Co-doped FeSiBC amorphous and nanocrystalline alloys

Tailoring the thermal stability and soft magnetic properties of Fe80-Ni Si7B8P4Cu1 amorphous nanocrystalline alloys based on the magnetic domain structure

Thermal and magnetic properties of Fe(Co)BCCu amorphous alloys with high saturation magnetization of 1.77 T

Magnetic properties and structure of short-term annealed FeCuBPSi nanocrystalline alloys

Effect of P microalloying on magnetic properties and structure of FeSiBNbCu nanocrystalline alloy

The influence of P on glass forming ability and clusters in melt of FeSiBP amorphous soft-magnetic alloy