Abstract:Insufficient performance, especially at high temperatures, limits the extensive application of cast Al–Cu alloys. This study proposes a novel method of direct reaction synthesis (DRS) for the simultaneous synthesis and dispersion of hybrid-sized in situ TiC–TiB2 particles in the melt to prepare a trace-particle-reinforced high-performance cast Al–Cu5.5–Mn0.45–Ti0.3–V0.3–Cr0.2–Zr0.14–B0.04 alloy. The particulate-reinforced alloy achieved strength–ductility synergetic enhancement at room and high temperatures. In comparison to the Al–Cu matrix alloy, the yield strength of 0.7 wt% (TiC–TiB2)/Al–Cu alloy at 298 K (529 MPa), 493 K (214 MPa), and 533 K (183 MPa) had an increase of 28%, 18% and 35%, meanwhile their elongation increased by 4%, 50% and 62%, respectively. The yield strength enhancement primarily benefited from the thermal mismatch between the particles and matrix, and Orowan strengthening. The strength–ductility performance improvement is due to the optimization of the microstructure: significantly refined α-Al grains with smaller and more dispersed θʹ precipitates. Further, the improvement mechanism of the microstructure is due to the action of the nanoparticles on the heterogeneous nucleation stimulation and dendrite growth inhibition of α-Al during the solidification process. Meanwhile, the segregation of the Cu atoms was inhibited by the particles. The precipitation was significantly promoted because of more uniformly distributed Cu atoms, and more defects induced by particles improved diffusion of the Cu atoms the number and density of the precipitation sites. The results of this study provide an economical and accessible synthesis strategy for industrial manufacturing.

Enhanced tensile properties in a Cu-Al2O3 alloy via trace Ti addition

Simultaneously Improved the Strength and Ductility of Cast Al-3Li-2Cu Alloy by Ti Addition and Heat Treatment

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Novel method to achieve synergetic strength–ductility improvement of Al–Cu alloy by in situ TiC–TiB2 particles via direct reaction synthesis

Synergistic enhancement of strength, ductility and corrosion resistance of Ti6Al4V alloy through low Cu doping and hot extrusion

Increased tensile strength and elongation of the Ni–Fe based polycrystalline cast superalloy via the trace addition of TiC nanoparticles

Effect of Ti addition on the mechanical properties and microstructure of novel Al-rich low-density multi-principal-element alloys

Microstructures and Mechanical Properties of Al–Zn–Mg–Cu Alloy with the Combined Addition of Ti and Zr

Influence of Ti Elements on the Evolution of Microstructure, Mechanical Properties and Thermal Stability of Al-Cu Alloy

Microstructure evolution and enhanced mechanical properties in Al-Mn alloy reinforced by B-doped TiC particles

Influence of Cu and Ti Microalloying on the Multiscale Microstructure Evolution and Mechanical Properties of 7xxx Alloys

Effect of Ti content on microstructure and properties of Al-9.9Zn-2.6Mg-0.91Cu-0.2Zr-xTi aluminum alloy

Enhancing strength-ductility synergy in nano-sized TiB 2 /Al composite via rapid solidification and thermo-mechanical processing

Microstructure and mechanical properties of Cu-12 Al-6 Ni with Ti addition prepared by powder metallurgy

Role of Ti in the Microstructure Evolutions and Mechanical Properties of Cast Al-2.5Li-1.5Cu-1Zn-0.5Mg(−0.2Zr) Alloys

Influence of TiCN addition on the microstructures and mechanical properties of the AZ31 alloy

Promoting Strengthening and Grain Refinement of Aluminum Alloy During Wire and Arc Additive Manufacturing by Adding TiB2 Particles

The Role of In-Situ Al3Ti Formed During Solidification in Improving the High-Temperature Properties of Al-Cu Alloy