Achieving high-temperature thermal evacuation between dissimilar materials C f /C and Mo30Cu by forming a brazed joint

Pengpeng Xue,Xiaoqing Si,Chun Li,Xiajun Guo,Wei Cai,Junlei Qi,Jian Cao

DOI: https://doi.org/10.1016/j.matchar.2023.113098

IF: 4.537

2023-06-20

Materials Characterization

Abstract:Achieving a high heat transfer is essential for the C f /C-Mo30Cu dissimilar material components in their applications of thermal nuclear reactions. In this study, the C f /C composite and the Mo30Cu alloy were successfully brazed by using the Ag-Cu-4.5Ti braze to eliminate interface gaps between them. The maximum thermal conductivity of the C f /C-Mo30Cu joint at 860 °C /10 min reached 112 W·m −1 ·K −1 (RT). The thermal conductivity of the joint even exceeds that of the C f /C matrix (107 W·m −1 ·K −1 ). It is worth noting that the overall thermal conductivity of the joint can still reach 92 W·m −1 ·K −1 at 500 °C. Shear test results showed that the average shear strength of the joints achieved 13.1 MPa at the highest thermal conductivity of the joint. A homogeneous TiC layer is generated along the C f /C interface, which is crucial for maintaining a stable joint and providing a favorable heat transfer channel across the C f /C-Mo30Cu dissimilar materials.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing