Abstract:This work successfully fabricated the fine-grained Mg-2.6Nd-0.55Zn-0.5Zr (wt%) alloy plates with the average grain sizes of 2.39–3.49 μm via the extrusion process. The microstructure evolution during extrusion process and the associated mechanical properties were investigated. Results showed that dynamic recrystallization (DRX) significantly refined the grain size and improved the microstructure homogeneity. Extrusion fragmentation effect on the coarse Mg12Nd particles contributed to the development of fine-grained uniform microstructure, especially at the lower extrusion temperature. Additionally, extrusion process turned the fiber basal texture into the double peak basal texture owing to the sequential deformation mode activation from basal slip and tension twinning to pyramidal <c+a> slip. Subsequent continuous DRX and particle-stimulated nucleation (PSN) recrystallization played a weakening effect on the double peak basal texture. Moreover, decreasing the extrusion temperature increased the activation difficulty of pyramidal <c+a> slip and weakened the effect of PSN on texture modification, leading the basal plane distribution along the extrusion direction to be strengthened. Fine-grained strengthening significantly improved the mechanical properties, but such strengthening capability was severely dependent on the texture. During tension deformation, the weak basal texture easily activated the basal slip whereas the strong basal texture needed to activate the prismatic slip. Hall-Petch analysis indicated that the higher yield stress in the strong basal texture was ascribed to the remarkable deformation mode strengthening (activation of prismatic slip) and the geometrical strengthening (higher Taylor factor). The weak basal texture was beneficial to improve the uniform elongation owing to the higher strain hardening ability, which was more obvious when the tension twinning was activated.

Evolution of Texture and Mechanical Anisotropy of Mg-13Gd-4Y-2Zn-0.5Zr Sheet Produced by Rotary Forward Extrusion

Formation of Abnormal Texture and Anisotropy Weakening Mechanism of Mg–Gd–Y–Zn–Zr Sheets by Rotary Forward Extrusion

Grain Refinement and Second Phases Evolution of Mg-13Gd-4Y-2Zn-0.4Zr Sheet During Processing by Rotary Forward Extrusion

Microstructure and Texture Evolution of Mg-Gd-Y-Zr Alloy during Reciprocating Upsetting-Extrusion

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Microstructure evolution, texture and mechanical properties of a Mg–Gd–Y–Zn–Zr alloy fabricated by cyclic expansion extrusion with an asymmetrical extrusion cavity: The influence of passes and processing route

Microstructure Evolution and Mechanical Properties of Mg-10.37Gd-3.66Y-2.27Zn-0.52Zr Alloy during Reciprocating Upsetting-Extrusion

Texture, microstructure and mechanical properties of an extruded Mg-10Gd-1Zn-0.4Zr alloy: Role of microstructure prior to extrusion

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Anisotropic cyclic deformation behavior of an extruded Mg-3Y alloy sheet with rare earth texture

Revealing the microstructure, texture evolution and mechanical properties along the whole wall of Mg-Gd-Y-Zn-Zr cylinders by tailoring rotary backward extrusion parameters

Texture role in the mechanical property improvement contributed by grain refinement for Mg-2.6Nd-0.55Zn-0.5Zr alloy subjected to extrusion process

Microstructure, Mechanical Properties, and Texture Evolution of Mg–Zn–Y–Zr Alloy Fabricated by Hot Extrusion–shearing Process

Microstructure, texture evolution and mechanical anisotropy of Mg-Gd-Y-Zn-Zr alloy sheets produced by unidirectional and cross rolling

Dynamic Recrystallization and Texture Evolution of Mg–Y–Zn Alloy During Hot Extrusion Process

The evolution of microstructure and texture of AZ80 Mg alloy cup-shaped pieces processed by rotating backward extrusion

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Effects of Extrusion Ratio on the Microstructure, Texture and Mechanical Properties of Mg-2.5Nd-0.5Zn-0.5Zr Alloy Sheets

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Analysis of Abnormal Texture Formation and Strengthening Mechanism in an Extruded Mg-Gd-Y-Zn-Zr Alloy