Abstract:The deformation of closed-cell aluminum foam (CAF) in different solid–liquid–gas coexisting state was studied in this paper. The results showed that the most suitable temperature of the CAF deformation was about 635 °C, which made the CAF have maximum deformation, but its characteristic parameters changed slightly. Moreover, the multi-grain cell wall and small size cell were helpful to the CAF deformation in the solid–liquid–gas coexisting state. When the CAF deformed at 635 °C, the inter-granular solidification microstructure and part of the primary α-Al grain were melted into liquid. The fixed or inter-locked primary α-Al grain was released and changed into the distributed discretely near-spherical grain, making the cell wall have good thixotropy. At the same time, the gas pressure in the cell was recovered to the foaming stage, so the gas pressure could be close to the flow stress of cell wall. During the CAF deformation in the solid–liquid–gas coexisting state, the cell wall deformed in thixotropic under the supporting and coordinating of the gas pressure in the cell, meanwhile, the cell was moved following the cell wall deformation. Therefore, the CAF deformation was affected by the types of the cell walls and the cell size. Graphic Abstract In this paper, the mold forming process was used to study the influence of temperature on deformation of the closed-cell aluminum foam (CAF) that in solid–liquid–gas coexisting state. When the CAF was deformed in solid–liquid–gas coexisting state who has strong deformation capacity, moreover, whose characteristic parameters are largely unchanged. However, shape forming of the closed cell aluminum foam only could be realized in specific solid–liquid–gas coexisting state, which was mainly related to the deformation temperature.

Fabrication of high-porosity open-cell aluminum foam via high-temperature deformation of CaCl2 space-holders

Fabrication of high-porosity open-cell aluminum foam via high-temperature deformation of CaCl<sub>2</sub> space-holders

Preparation and Compression Behavior of High Porosity, Microporous Open-Cell Al Foam Using Supergravity Infiltration Method

Fabrication and Compressive Behavior of Open-Cell Aluminum Foams Via Infiltration Casting Using Spherical CaCl2 Space-Holders

Pore Structure and Compressive Properties of Open-Cell Aluminum Foams Prepared by Infiltration Casting Based on NaCl Space-Holder

Manufacturing of open-cell aluminum foams via infiltration casting in super-gravity fields and mechanical properties

Effect of Precursor Design on Preparing Open-Cell Aluminum Foam Fabricated by Space-Holder Method

Study on Deformation of Closed-Cell Aluminum Foam in Different Solid–Liquid–Gas Coexisting State

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Shape Formation of Closed-Cell Aluminum Foam in Solid–liquid–gas Coexisting State

Fabrication of Uniform and Rounded Closed-Cell Aluminum Foams Using Novel Foamable Precursor Particles (FPPs)

Preparation of Aluminum Foam by Gas Injection Foaming

Multifunctional Open-Cell Copper Foam with Sphere Pores by a Modified Sintering–Dissolution Process

Preparation of complex shaped aluminum foam by a novel casting-foaming method

Low-Temperature Reactive Sintered Porous Mg-Al-Zn Alloy Foams

Optimizing Calcium Addition for Fabricating Aluminum Foams with Different Pore Sizes

Investigation on the Structural and Mechanical Properties of Al Foam Manufactured by Spark Plasma Sintering and Compression Molding Methods

Preparation of Shaped Aluminum Foam Parts by Investment Casting

Fabrication of Al Foam Without Thickening Process Through Melt-Foaming Method

Fabrication and characterization of aluminum foam reinforced with nanostructured γ-Al2O3 via friction stir process for enhanced mechanical performance

Mesostructural Design and Manufacturing of Open-Pore Metal Foams by Investment Casting