Abstract:Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

Shape Formation of Closed-Cell Aluminum Foam in Solid–liquid–gas Coexisting State

Study on Deformation of Closed-Cell Aluminum Foam in Different Solid–Liquid–Gas Coexisting State

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Solidification microstructure and grain refinement of closed-cell aluminum foams

Preparation of Aluminum Foam by Gas Injection Foaming

Foaming Behavior of Microsized Aluminum Foam Using Hot Rolling Precursor

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Study on an Aluminum Foam by Gas Injection Foaming

Preparation principle and compression properties of cellular Mg–Al–Zn alloy foams fabricated by the gas release reaction powder metallurgy approach

Early Compressive Deformation of Closed-Cell Aluminum Foam Based on a Three-Dimensional Realistic Structure

Preparation and Compression Behavior of High Porosity, Microporous Open-Cell Al Foam Using Supergravity Infiltration Method

Manufacturing of open-cell aluminum foams via infiltration casting in super-gravity fields and mechanical properties

Fabrication and Compressive Behavior of Open-Cell Aluminum Foams Via Infiltration Casting Using Spherical CaCl2 Space-Holders

The influence of process parameters on the preparation of closed-cell aluminum foam by friction stir processing

The Influences of Process Parameters on the Preparation of Closed-cell Aluminum foam by Friction Stir Processing

Characterization of as-cast microstructure of aluminum foams by melt foaming method

Effect of Precursor Design on Preparing Open-Cell Aluminum Foam Fabricated by Space-Holder Method

The influence of pure Al and hypoeutectic Al Si alloy base materials on the cell structures of aluminum foams produced by gas injection foaming process

Fabrication, Processing, Properties, and Applications of Closed-Cell Aluminum Foams: A Review

Preparation of Shaped Aluminum Foam Parts by Investment Casting

Modeling of Macro-Deformation Behavior of Thin-Walled Aluminum Foam by Gas Injection Method