Preparing ribbons with core@shell columnar structures and high magnetization using phase transition decomposition mechanism

Hang-Qian Zhang,Ji-Bing Sun,Mu-Jing Zhou,Si-Yi Chen,Hao-Yu Ma,Yu-Long Liu

DOI: https://doi.org/10.1016/j.jallcom.2024.173815

IF: 6.2

2024-04-01

Journal of Alloys and Compounds

Abstract:A new way to prepare soft magnetic materials with high magnetization was proposed using the phase transition decomposition theory, and the saturated magnetic polarization intensity of the ribbons designed based on the composition of FeCo-type α1 phase reaches 1.88 T after melt-spinning at 40 m/s. The ingots and as-spun ribbons comprise FeCo-type main and AlNi-type minor phases. During melt-spinning, the main phase grows into columnar grains along the thickness direction of the as-spun ribbons. AlNi phase distributes at the grain boundaries of the columnar grains, and its content reduces from 38.8 wt% to 22.0 wt%, thus forming a novel core@shell columnar structure. The micromagnetic simulation results revealed that the soft magnetic properties of as-spun ribbons with AlNi phase at the grain boundaries are superior to that of the nonmagnetic grain boundary phase and grain boundary-free models. The weakly magnetic AlNi phase promotes the coordinated rotation of the magnetic moments of the ferromagnetic FeCo phase within the grains, thus reducing the coercivity of the ribbons; the columnar grain structure improves the remanence of the as-spun ribbons. This FeCo@AlNi core-shell columnar structure provides a new idea for preparing soft magnetic materials with high magnetization.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering