Abstract:A high conversion efficiency (η) of 13% was achieved with a hot‐side temperature (Th) of 500 °C and cold‐side temperature (Tc) of about 5 °C. The thermoelectric device showed a stable η of over 100 h at Th and Tc of 400 and 5 °C, respectively. Realizing high‐temperature thermal stability in thermoelectric (TE) generators is a critical challenge. In this study, a synergistic interface and surface optimization strategy is implemented to enhance Mg3Sb1.5Bi0.5 TE generator performance by employing FeCrTiMnMg thermoelectric interface materials and the MgMn‐based alloy protective coating. The competitive output power density (ω) of 1.7 W cm−2 and a conversion efficiency (η) of 13% for the single‐leg device are achieved at hot‐side temperature (Th) and cold‐side temperature (Tc) of 500 and 5 °C, respectively. An ω of 0.8 W cm−2 and η of 6% for the two‐couple TE devices with p‐type commercial Bi2Te3 are also realized, values that are competitive with the commercial Bi2Te3 device. Additionally, the single‐leg device shows a high stable η for over 100 h when the Th and Tc are 400 and 5 °C, respectively, with an change rate (Δηmax/ηmax,o) of <3%. In situ transmission electron microscopy analysis further reveals that the high stability results from the effectively sluggish interdiffusion and reduced Mg evaporation that decrease the chemical potential gradient, reduce the saturated vapor pressure, and increase the diffusion activation energy barrier. This study provides a general technique route for boosting the high‐temperature thermal stability of TE generator.

Orientation optimization for high performance Mg3Sb2thermoelectric films via thermal evaporation

Orientation Optimization for High Performance Mg3sb2 Thermoelectric Films Via Thermal Evaporation

Improved performance in Mg3Sb2/Sb hybrid films for thermoelectric generation

High‐Performing Flexible Mg3Bi2 Thin‐Film Thermoelectrics

High-Performance Mg<sub>3</sub>Sb<sub>2-<i>x</i></sub>Bi<i><sub>x</sub></i> Thermoelectrics: Progress and Perspective

Electronic Orbital Alignment and Hierarchical Phonon Scattering Enabling High Thermoelectric Performance p-Type Mg 3 Sb 2 Zintl Compounds

Interface and Surface Engineering Realized High Efficiency of 13% and Improved Thermal Stability in Mg3Sb1.5Bi0.5‐Based Thermoelectric Generation Devices

Effect of Annealing Conditions on Thermoelectric Properties of Magnetron Sputtered MgO-Ag3Sb-Sb2O4 Flexible Films

High-performance Mg3Sb2-based thermoelectrics with reduced structural disorder and microstructure evolution

Interfacial Design Contributing to High Conversion Efficiency in Mg3(Sb, Bi)2/Bi2Te3 Thermoelectric Module with Superior Stability

Enhancement of ZT in Bi0.5Sb1.5Te3 Thin Film through Lattice Orientation Management

In situ crystal-amorphous compositing inducing ultrahigh thermoelectric performance of p-type Bi0.5Sb1.5Te3 hybrid thin films

Synergistic Texturing and Bi/Sb‐Te Antisite Doping Secure High Thermoelectric Performance in Bi 0.5 Sb 1.5 Te 3 ‐Based Thin Films

Mg3(Bi,Sb)2 single crystals towards high thermoelectric performance

Carrier concentration and orientation optimization for high performance (Sb,Bi) 2 Te 3 thermoelectric films via magnetron co-sputtering

Epitaxial growth of high-quality Mg 3 Sb 2 thin films on annealed c-plane Al 2 O 3 substrates and their thermoelectric properties

High thermoelectric performance and anisotropy studies of n-type Mg3Bi2-based single crystal

High-Performance Mg3Sb2-xBix Thermoelectrics: Progress and Perspective

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Improving Thermoelectric Performance Of Alpha-Mgagsb By Theoretical Band Engineering Design

High-Performance Low-Cost n-Type Se-Doped Mg3Sb2-Based Zintl Compounds for Thermoelectric Application