Abstract:A range of Fe-Cr-Ni alloys are used in nuclear power plants due to their high mechanical strength and corrosion resistance. As a major component of these alloys, Ni contributes to the formation of austenite microstructures. In many nuclear reactor applications the alloys are exposed to ionizing radiation (g-rays) that can continuously decompose water to a range of highly redox active species (such as •OH, H2O2, O2). The change in water chemistry induced by radiation can affect both the general and localized corrosion behaviour of these alloys. In particular, its influence on the susceptibility of an alloy to localized corrosion such as crevice and stress corrosion cracking (SCC) are important for assessment of reactor component aging. As well, corrosion products that dissolve into the reactor coolant can be transported to the reactor core where they can be neutron activated. This can create a radiological hazard for reactor maintenance personnel. Thus, quantifying the rate of general corrosion and the corrosion product transport in a reactor are important safety, operation and maintenance issues. It has been well established that the type of oxide that forms on a surface is a critical factor in determining both general and localized corrosion behaviour. Both alloy composition and water chemistry affect the type of oxide that forms. Systematic studies that examine the effect of alloy composition on corrosion are rare and those available have been conducted mostly from a metallurgical perspective. There are even fewer studies that examine the combined effects of alloy composition and corrosion environment. A fundamental understanding of the mechanism by which the Fe to Ni ratio in a steel alloy influences the corrosion rate in different environments will provide valuable information that can be used for alloy selection and usage. We have investigated the effect of the Fe to Ni ratio of alloy on oxide formation and growth kinetics. For this study, customized steel alloys with different Ni contents and constant Cr content (18 ± 1 %) were prepared. The Ni content ranged from 15 to 25 wt.%, within the range between AISI 316L and Alloy 800 (Fig. 1). The corrosion kinetics was investigated using a combination of coupon corrosion tests and electrochemical measurements. These measurements were augmented by oxide surface and depth analyses using several spectroscopic and imaging techniques, and by post-test solution analyses for dissolved metal loss. We found that the oxide formed at pH 10.6 and 80 °C has a graded layer structure, consisting of a mixed spinel oxide (FeCr2O4/Fe3O4/NiFe2O4) as an inner layer and Ni(OH)2 as an outer layer. The increase in Ni content from 15 to 25 wt.% does not affect the inner layer but increases the thickness of the Ni(OH)2 layer. The increase in Ni content also decreases the total amount of dissolved metal loss. Gamma-irradiation of the corroding system increases the corrosion potential on these alloys. Correspondingly, gamma-radiation accelerates the formation of passive oxide layers and decreases the overall rate of metal dissolution. The observed kinetics of oxide growth and metal dissolution can be explained by the competition kinetics of oxide growth and dissolution for oxidized metals. Figure 1

Effect of N and Nb Microalloying on Corrosion Resistance of 309S Stainless Steel for Canister-Stored Nuclear Waste

Effect of Nb addition on the microstructure and corrosion resistance of ferritic stainless steel

Effect of Tensile Deformation on Microstructure and Corrosion Resistance of High Nitrogen Austenitic Stainless Steels

Corrosion behaviour of nanocrystallines 304 stainless steel in simulated secondary side environment

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Corrosion Behavior of Alumina-Forming Austenitic Steel in Supercritical Carbon Dioxide Conditions: Effects of Nb Content and Temperature

Effects of composition and microstructure on oxidation and stress corrosion cracking susceptibility of stainless steel claddings in hydrogenated PWR primary water

Effect of Sulfide and Chloride Ions on Pitting Corrosion of Type 316 Austenitic Stainless Steel in Groundwater Conditions Using Response Surface Methodology

Effect of heavy ion irradiation on the electrochemical behavior of 321 stainless steel

Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Effect of Nickel Content on the Corrosion Behaviour of Stainless Steel at 80 °C

The Microstructure and Mechanical and Corrosion Behaviors of Thermally Aged Z3CN20-09M Cast Stainless Steel for Primary Coolant Pipes of Nuclear Power Plants

Influence of Nb on the Hot Corrosion Behaviors of a Fe–Cr–Ni Heat-Resistant Steel Weld Metal in the Na2SO4–NaCl Molten Salt at 700 °C

Electrochemical corrosion of multiphase stainless steel-based alloy nuclear waste forms

Effect of Nb Substitution for Cu on Glass Formation and Corrosion Behavior of Zr Cu Ag Al Be Bulk Metallic Glass

Comparative studies on microstructure evolution and corrosion resistance of 304 and a newly developed high Mn and N austenitic stainless steel welded joints

INFLUENCE OF NIOBIUM AND NITROGEN ON THE RESISTANCE TO PITTING AND INTERGRANULAR CORROSION OF 304 AUSTENITIC STAINLESS STEEL

Microstructure, mechanical properties and tribo-corrosion mechanism of (CrNbTiAlVMo) x N 1-x coated 316 L stainless steel in 3.5 wt.% NaCl solution

Effect of Alloying Elements and Low Temperature Plasma Nitriding on Corrosion Resistance of Stainless Steel

The effect of Nb content on microstructure and properties of laser cladding 316L SS coating