Abstract:The Ti-based bulk metallic glasses (BMG) with high Ti content (>50 at.%) have attracted wide attention for their outstanding mechanical properties, despite their glass forming ability (GFA) is still relatively poor. Here the (Ti55Zr15Be20Ni10)(100-x)Cu-x(x = 2, 4, 6, 8 and 10 at.%) BMGs were designed and prepared by copper mold casting. The critical diameter of the original alloy could be enhanced from 5 mm to 10 mm with the Cu addition of 4 at.%, which is the first reported centimeter-sized Ti-based BMG with Ti content more than 52 at.%. In addition, all the as-prepared BMGs exhibited higher yield strength (above 2000 MPa). And the supercooled liquid range of the as-prepared Ti-based BMGs were enlarged from 35 K to 74 K by Cu addition. Electrochemical measurements showed that the BMGs with Cu addition of 0-6 at.% exhibited much higher pitting potentials (over 573 mV/SCE) than that of 304 stainless steel (304SS) in 3.5 wt% NaCl aqueous solution. And The XPS analysis revealed that the Cu addition might lead to the enrichment of Cu and the deficiency of Ti, Zr, Ni elements in passive film, which could induce the worse corrosion resistance of the Ti-based BMGs with high Cu content. The results indicate that the developed Ti-based BMGs possess good GFA, mechanical properties and corrosion resistance. (C) 2017 Elsevier B.V. All rights reserved.

Effect of Nb Substitution for Cu on Glass Formation and Corrosion Behavior of Zr Cu Ag Al Be Bulk Metallic Glass

Effect of Nb and Cu on α/β Phase Transition Temperature and Corrosion Behavior of New Type Zirconium Alloys

Effect of Thermal Oxidization on Corrosion Behavior of Zr-based Bulk Metallic Glass

The effect of Nb addition on mechanical properties, corrosion behavior, and metal-ion release of ZrAlCuNi bulk metallic glasses in artificial body fluid

Corrosion behavior, mechanical properties and cell cytotoxity of Zr-based bulk metallic glasses

Corrosion mechanisms of Zr-based bulk metallic glasses in NaBr solution

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys

Effects of Ca addition on the glass formation, microhardness and corrosion resistance in different solutions of Zr66.7- xNi33.3Cax (x = 0, 1, 3 and 5 at.%) metallic glasses

Effect of Al addition on properties of Cu45Zr45.5Ti9.5 bulk metallic glass

Effects of Nb Addition on Icosahedral Quasicrystalline Phase Formation and Glass-Forming Ability of Zr–Ni–Cu–Al Metallic Glasses

Electrochemical and XPS studies of a Nb-containing Ti-based glass-forming alloy system in H 2 SO 4 solution

Glass formation, corrosion behavior and mechanical properties of bulk glassy Cu–Hf–Ti–Nb alloys

Glass Forming Ability and Corrosion Resistance of Zr-Cu- Ni-Al-Ag Bulk Metallic Glass

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

The Effect of Oxidation on the Corrosion Resistance and Mechanical Properties of A Zr-Based Metallic Glass

Ti Microalloying Effect on Corrosion Resistance and Thermal Stability of CuZr-based Bulk Metallic Glasses

Thermal Oxidation Effect on Corrosion Behavior of Zr46Cu37.6Ag8.4Al8 Bulk Metallic Glass

Glass formation, chemical properties and surface analysis of Cu-based bulk metallic glasses

Effect of Nb in (La0.5ce0.5)(64-X)al16ni5cu15nbx (X=0-5) Bulk Metallic Glasses

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Effects of adding niobium on microstructures and mechanical properties of ((Zr40Ti40Ni20)72Be28)100-Nb bulk metallic glasses