An origin of corrosion resistance changes of Zr alloys: effects of Sn and Nb on grain boundary strength of surface oxide

Rong Yuan,Yao-Ping Xie,Tong Li,Chen-Hao Xu,Mei-Yi Yao,Jing-Xiang Xu,Hai-Bo Guo,Bang-Xin Zhou
DOI: https://doi.org/10.1016/j.actamat.2021.116804
IF: 9.4
2021-05-01
Acta Materialia
Abstract:<p>As nuclear fuel cladding, Zr alloys have need for a good corrosion resistance. For decades, several generations of Zr alloys with excellent corrosion resistance have been developed through adjusting content of Sn and Nb. However, the mechanism of Sn and Nb influencing the corrosion resistance is still not clear. Here, our computational simulations indicate, Sn or Nb can segregate at grain boundary (GB) of surface oxide film which results in variation of GB cohesion and influences the corrosion resistance. Using the first-principles method, we find that Sn segregation reduce GB cohesion and decrease oxide film protectiveness; In contrast, Nb segregation enhance GB cohesion and improve oxide film protectiveness. The results are well consistent with the previous experiments that reducing Sn or adding Nb can promote corrosion resistance of Zr alloys. These findings provide a basis for understanding the roles of alloying elements in the corrosion resistance of Zr alloys, which is useful to future design of new Zr alloys.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper aims to address the corrosion resistance issue of zirconium alloys (Zr alloys) used in nuclear fuel cladding materials. Specifically, it seeks to improve the corrosion resistance of Zr alloys by adjusting the content of alloying elements tin (Sn) and niobium (Nb). However, the specific mechanisms by which Sn and Nb affect corrosion resistance are not yet clear. The paper investigates the segregation effects of Sn and Nb at the grain boundary (GB) of the surface oxide film and their impact on grain boundary cohesion through computational simulations, thereby exploring how these factors influence corrosion behavior. The main findings include: - Sn segregation reduces grain boundary cohesion, thereby decreasing the protective nature of the oxide film. - Conversely, Nb segregation enhances grain boundary cohesion, improving the protective nature of the oxide film. These results are consistent with previous experimental observations that reducing Sn or adding Nb can improve the corrosion resistance of Zr alloys. These findings provide a basis for understanding the role of alloying elements in the corrosion resistance of Zr alloys and offer guidance for the future design of new Zr alloys.