Abstract:In this paper, the ultrasonic shot peening (USSP) technology was used to obtained surface nanocrystalline of 20 carbon steel. The grain size of test surface and the thickness of nanocrystallization layer were analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). The three electrode electrochemical measurement was employed to investigate the electrochemical corrosion performance and the critical character of USSP surface nanocrystallization samples in different impact strength. The results showed that the USSP surface nanocrystallization could obtain the nanocrystalline grain. The thickness of nanocrystallization layer increased and grain sizes reduced with the increase of the impact strength. Nanocrystallization layer took the way to expand concentric circles with impact crater as the center. The corrosion current of nanocrystallization sample was much larger than as-received. The controlled step of corrosion process was turned from cathodic process to anodic process by USSP surface nanocrystallization. The sample surface formed two layers corrosion product films in condensate water, which were compact Fe3O4 membrane as inner corrosion product film and loose Fe3O4 membrane or Fe2O3 membrane as outer layer. With the increase of the impact strength, critical velocity of the outer corrosion product film increased gradually. The critical velocity of inner corrosion product film had an increasing trend, but the critical velocity tended to be a constant value when impact strength was more than 1.9904min/cm(2).

Corrosion behaviour of nanocrystallines 304 stainless steel in simulated secondary side environment

Corrosion Behaviour of Nanocrystallines Alloy 690 at High-Temperature and High-Pressure in Simulated PWR Secondary Environment

Anti-corrosion and corrosive wear properties of AISI 316L stainless steel with surface nanocrystallization by surface mechanical rolling treatment

Errosion-Corrosion Critical Performance of Surface Nanocrystalline 20 Carbon Steel in Condensate Water

Corrosion behaviour of nanocrystalline 304 stainless steel prepared by equal channel angular pressing

CORROSION BEHAVIORS OF NUCLEAR-GRADE STAINLESS STEEL AND FERRITIC-MARTENSITIC STEEL IN SUPERCRITICAL WATER

Microstructure Characteristic and Electrochemical Corrosion Behavior of Surface Nano-crystallization Modified Carbon Steel

Assessing the tribo-corrosion resistance of surface nanostructured stainless-steel

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

A High-Resolution Study of the Different Surface State Effects on the Corrosion Behaviors of a Ferritic Steel and an Austenitic Steel in Supercritical Water

In Vitro Corrosion and Haemocompatibility of Bulk Nanocrystalline 304 Stainless Steel by Severe Rolling

Nanocrystallization Technology and Corrosion Resistance of Stainless Steel

Corrosion Behavior and Mechanism of Irradiated 304 Nuclear Grade Stainless Steel in High-Temperature Water

Effects of Surface Nano-crystallization on Mechanical Properties of 304 Stainless Steel/CrN Film

Effect of surface nanocrystallization induced by mechanical grinding treatment on stress corrosion cracking behavior of 316 L austenitic stainless steel in boiling MgCl 2 solution

Enhance corrosion resistance of 304 stainless steel using nanosecond pulsed laser surface processing

Enhanced Mechanical Properties and Corrosion Resistance of 316l Stainless Steel by Pre-Forming a Gradient Nanostructured Surface Layer and Annealing

Effect of Irradiation on Corrosion of 304 Nuclear Grade Stainless Steel in Simulated PWR Primary Water

Structure and Mechanical Properties of Liquid Nitrocarburized 304 Stainless Steel with a Nanocrystalline Surface Layer

Effect of nanocrystallization on the corrosion behavior of low carbon steel

Corrosion Mechanisms of Stainless Steel and Nickel Base Alloys in High Temperature High Pressure Water