Abstract:Journal of Composite Materials, Ahead of Print. Laminates are produced by stacking prefabricated plies composed of fiber products. Within the aerospace industry, a ply thickness of 125 μm is commonly regarded as the standard. Ply thicknesses of less than 100 μm are generally considered as thin plies. Due to their ability to provide superior mechanical properties relative to conventional laminates thin-ply (TP) laminates are gaining interest in several high-tech industries. Although the research on TP laminates increased over the past few years, a comprehensive evaluation of the mechanical behavior of TP laminates accounting for the ply-thickness is an ongoing challenge due to the intricacies of ply interactions, and experimental difficulties. The mechanical response of fiber reinforced polymer laminates is governed by damage progression during loading, with the thickness of individual plies playing a crucial role in influencing the initiation and evolution of local cracks and failures. Therefore, in this study, the effective mechanical properties of carbon fiber reinforced polymer composite with varied ply thicknesses have been experimentally evaluated and the accumulation of the damage events has been monitored using acoustic emission measurements, utilizing a contactless laser vibrometer. In this experimental study, the ply thickness is increased in a systematic manner (ranging from 50 μm to 200 μm). Experimental investigation has been carried out in quasi-static tension and compression. The results show that unnotched TP laminates subjected to tensile loading demonstrate enhanced effective strength, attributed to less premature failure. Conversely, as the thickness of the lamina increases, there is a reduction in the overall strength of the laminate. However, in the case of the notched specimen lowest strength has been observed at a ply-thickness of 100 μm in this study. Under compressive loading, unnotched and notched specimen tends to show similar mechanical behavior to unnotched specimens under tensile loading. The overall strength is raised with decreasing ply thickness. The findings from this study may be valuable for incorporating ply-thickness considerations into models for predicting the mechanical performance of laminates under dynamic loading.

Study on biaxial tensile failure behavior of ultra-thin-ply carbon fiber reinforced composites

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Thickness Variation Effect on Compressive Properties of Ultra-Thick CFRP Laminates

Experimental and theoretical investigation on tensile properties and fracture behavior of carbon fiber composite laminates with varied ply thickness

Biaxial tensile failure of short carbon-fibre-reinforced PEEK composites

Failure behavior and damage visualization of thick carbon/aramid hybrid woven composites under flexural loading conditions

Experimental Study on the Mechanical Behavior and Failure Mechanism of 3d MWK Carbon/epoxy Composites under Quasi-Static Loading

Analysis of in-plane compression failure mechanism in carbon fiber braided composite with different off-axial angles

Comprehensive inter-fibre failure analysis and failure criteria comparison for composite materials using micromechanical modelling under biaxial loading

Effect of triaxial woven fabric on bending properties of unidirectional composites

A Study on the Intralaminar Damage and Interlaminar Delamination of Carbon Fiber Composite Laminates under Three-Point Bending Using Acoustic Emission

Experimental and numerical study of in-plane compressive properties and failure of 3D six-directional braided composites with large braiding angle

Evaluating the mechanical behavior of carbon composites with varied ply-thicknesses using acoustic emission measurements

Multiaxial failure mechanism of 3D triple-twill warp-lining woven composites

Experimental and simulation study on compressive failure evolution of multidirectional laminates with different dimensions

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Flexural progressive damage and failure behavior of carbon-aramid/epoxy hybrid woven composites

Elastic and Fracture Behavior of Three-Dimensional Ply-to-Ply Angle Interlock Woven Composites: Through-Thickness, Size Effect, and Multiaxial Tests

Fracture toughness and fiber bridging mechanism for mode-I interlaminar failure of spread-tow woven composites

Exploring the influence of specimen types on the intralaminar fracture behavior of fiber-reinforced polymer matrix composites

Experimental investigation on mechanical response and failure analysis of 3D multi-axial warp knitted hybrid composites