Abstract:Huge amount of flue gas desulphurization (FGD) gypsum not only occupies the farmland but also causes severe pollution to the surrounding environment. The most effective way to achieve a high-value utilization of FGD gypsum is to prepare short columnar α-calcium sulfate hemihydrate (α-HH) since short columnar crystals show better mechanical strength than needle-like ones. Here, malic acid, a prolific, inexpensive and environment-friendly modifier was explored for the first time to effectively tune the crystal morphology of α-HH prepared from FGD gypsum in glycerol-water-NaCl solutions. When the concentration of malic acid reached 18.54 × 10-4 mol/kg, α-HH crystals with an average aspect (length-to-diameter) ratio of 1.9 (compared to 29.4 in the absence of malic acid) were prepared. The selective complexation of malic acid with Ca active sites on different α-HH crystal planes played a dominant role in the α-HH crystal morphology transformation, which was then explained by the surface broken bonds theory for the first time. The broken bond number per active Ca atom (Nbper Ca) and broken bond density of Ca atoms (DbCa) on the (2 0 4) end plane were larger than those on the (0 2 0) or (2 0 0) side planes. Therefore, the (2 0 4) end plane was more reactive with organics, resulting in the preferential adsorption of malic acid on the end planes, which reduced the specific surface energy of (2 0 4) and led to an increased exposure of this plane and a decreased exposure of (0 2 0) or (2 0 0) side planes in the final α-HH crystals. Consequently, using malic acid as modifier, the α-HH crystal gradually transformed from a needle-like shape to a short columnar one. This work provided important insights into and perspectives for the selection of crystal modifiers and explanation of the mechanism during the preparation of calcium-containing crystals with controllable morphology.

α-calcium sulfate hemihydrate preparation from FGD gypsum in recycling mixed salt solutions

Pilot scale preparation of α-calcium sulfate hemihydrate from FGD gypsum in Ca–K–Mg aqueous solution under atmospheric pressure

Characterization and Precipitation Mechanism of Α-Calcium Sulfate Hemihydrate Growing out of FGD Gypsum in Salt Solution

Modification of FGD Gypsum in Hydrothermal Mixed Salt Solution.

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Facile preparation of α-calcium sulfate hemihydrate whisker from by-product gypsum in chloride-free salt solution system

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Influence of Seed Crystal and Modifier on the Morphology of α-calcium Sulfate Hemihydrate Prepared by Salt Solution Method in Pilot Scale

Preparation of α-High Strength Gypsum from Flue Gas Desulfurization Gypsum Pretreated by Hydrothermal-aging Method

Preparation of α-hemihydrate gypsum from phosphogypsum in recycling CaCl2 solution

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste

Preparation of calcium sulfate from recycled red gypsum to neutralize acidic wastewater and application of high silica residue

Preparation of α-calcium sulfate hemihydrate from industrial by-product gypsum: A review

Transformation of flue-gas-desulfurization gypsum to (α-hemihydrated gypsum in salt solution at atmospheric pressure

Retarding effect of impurities on the transformation kinetics of FGD gypsum to α-calcium sulfate hemihydrate under atmospheric and hydrothermal conditions

Preparation of α-CaSO4·½H2O with tunable morphology from flue gas desulphurization gypsum using malic acid as modifier: A theoretical and experimental study