Abstract:Huge amount of flue gas desulphurization (FGD) gypsum not only occupies the farmland but also causes severe pollution to the surrounding environment. The most effective way to achieve a high-value utilization of FGD gypsum is to prepare short columnar α-calcium sulfate hemihydrate (α-HH) since short columnar crystals show better mechanical strength than needle-like ones. Here, malic acid, a prolific, inexpensive and environment-friendly modifier was explored for the first time to effectively tune the crystal morphology of α-HH prepared from FGD gypsum in glycerol-water-NaCl solutions. When the concentration of malic acid reached 18.54 × 10-4 mol/kg, α-HH crystals with an average aspect (length-to-diameter) ratio of 1.9 (compared to 29.4 in the absence of malic acid) were prepared. The selective complexation of malic acid with Ca active sites on different α-HH crystal planes played a dominant role in the α-HH crystal morphology transformation, which was then explained by the surface broken bonds theory for the first time. The broken bond number per active Ca atom (Nbper Ca) and broken bond density of Ca atoms (DbCa) on the (2 0 4) end plane were larger than those on the (0 2 0) or (2 0 0) side planes. Therefore, the (2 0 4) end plane was more reactive with organics, resulting in the preferential adsorption of malic acid on the end planes, which reduced the specific surface energy of (2 0 4) and led to an increased exposure of this plane and a decreased exposure of (0 2 0) or (2 0 0) side planes in the final α-HH crystals. Consequently, using malic acid as modifier, the α-HH crystal gradually transformed from a needle-like shape to a short columnar one. This work provided important insights into and perspectives for the selection of crystal modifiers and explanation of the mechanism during the preparation of calcium-containing crystals with controllable morphology.

Modification of FGD Gypsum in Hydrothermal Mixed Salt Solution.

Transformation of flue-gas-desulfurization gypsum to (α-hemihydrated gypsum in salt solution at atmospheric pressure

α-calcium sulfate hemihydrate preparation from FGD gypsum in recycling mixed salt solutions

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Characterization and Precipitation Mechanism of Α-Calcium Sulfate Hemihydrate Growing out of FGD Gypsum in Salt Solution

Retarding effect of impurities on the transformation kinetics of FGD gypsum to α-calcium sulfate hemihydrate under atmospheric and hydrothermal conditions

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

Pilot scale preparation of α-calcium sulfate hemihydrate from FGD gypsum in Ca–K–Mg aqueous solution under atmospheric pressure

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Influence of Seed Crystal and Modifier on the Morphology of α-calcium Sulfate Hemihydrate Prepared by Salt Solution Method in Pilot Scale

Preparation of α-CaSO4·½H2O with tunable morphology from flue gas desulphurization gypsum using malic acid as modifier: A theoretical and experimental study

Direct transformation of calcium sulfite to α-calcium sulfate hemihydrate in a concentrated Ca–Mg–Mn chloride solution under atmospheric pressure

Experimental Studies on Decomposing Properties of Desulfurization Gypsum in a Thermogravimetric Analyzer and Multiatmosphere Fluidized Beds

Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste

A Feasible Route for Preparation of Calcium Sulfate Whiskers from FGD Gypsum via Filtrate Recycle under Hydro-Thermal Conditions

Research on Saline-Alkali Soil Amelioration with FGD Gypsum

Utilizations of preheated flue gas desulfurization gypsum and sulfate compositions to modify performances of super-sulfated cement

Preparation of calcium sulfate from recycled red gypsum to neutralize acidic wastewater and application of high silica residue