Abstract:α-hemihydrate (α-HH), known for its exceptional mechanical properties, is a widely used building material. Despite its advantages, the traditional method of producing α-HH through regular pressure brine poses significant drawbacks. These include substantial industrial salt demands, high production costs, and water pollution. A more environmentally friendly α-HH preparation process has been developed to counteract these issues, combining FGD gypsum and concentrated brine. This study delves into the effects of the principal ions present in concentrated brine on the phase transition process and the microstructure of the final product. Our findings reveal that the reaction rate accelerates with increased concentrations of Ca2+, Mg2+, K+, and Na+ in concentrated brine. However, excessive Na+ concentration can alter the phase transition process, converting the product to β-HH. Additionally, an overly high concentration of KCl may prompt a part of the K+ to engage in the reaction, leading to the formation of isomeric potassium gypsum. This process can disrupt the original structure of hemihydrate gypsum. The addition of maleic acid to the salt solution was found to foster anhydrous gypsum formation. In contrast, succinic acid can decrease the crystals' aspect ratio, resulting in the growth of short columns, thereby enhancing the product's strength performance. Our research also identified that the reaction rate elevates as the pH value declines. However, an acidic environment diminishes the size of the crystal and counteracts the crystal modifier's effects. Lastly, incorporating CaCl2 and MgCl2 into concentrated brine with a low Na+ concentration can convert FGD gypsum into high-strength α-HH. This transformation results in a product boasting a 1-day compressive strength of 40.5 MPa.

Retarding effect of impurities on the transformation kinetics of FGD gypsum to α-calcium sulfate hemihydrate under atmospheric and hydrothermal conditions

Effect of particle size on the transformation kinetics of flue gas desulfurization gypsum to α-calcium sulfate hemihydrate under hydrothermal conditions

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Insights into the Role of Na+ on the Transformation of Gypsum into Α-Hemihydrate Whiskers in Alcohol–Water Systems

Modification of FGD Gypsum in Hydrothermal Mixed Salt Solution.

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

Influence of crystal-transforming agent on the performance and mechanism of α-high-strength gypsum prepared from FGD gypsum

Characterization and Precipitation Mechanism of Α-Calcium Sulfate Hemihydrate Growing out of FGD Gypsum in Salt Solution

A readily monitored and controllable hydrothermal system for the facile, cost-effective transformation of FGD gypsum to calcium sulfate hemihydrate whiskers

Effect of Ph on the Preparation of Alpha-Calcium Sulfate Hemihydrate from Fgd Gypsum with the Hydrothermal Method

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Efficient removal of impurities from phosphogypsum during preparation of α-hemihydrate gypsum

Effect of Al2(SO4)3 Additive on the Properties of Calcined Gypsum Prepared from Flue Gas Desulfurization

Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers: Preparation, simulations, and process analysis

Efficient precipitation of soluble phosphorus impurities in the recycling of phosphogypsum to produce hemihydrate gypsum

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

A Feasible Route for Preparation of Calcium Sulfate Whiskers from FGD Gypsum via Filtrate Recycle under Hydro-Thermal Conditions

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum