Influence of Carbon and Pyrite on Desulfurization Behavior of Red Gypsum at High Temperature
Ma Xiaoling,Tan Hongbin,Dong Faqin,Yang Feihua
DOI: https://doi.org/10.1007/s40831-021-00483-8
2022-01-01
Journal of Sustainable Metallurgy
Abstract:Red gypsum is generated from TiO2 production industry by the sulfate method, which contains iron, calcium, and sulfur elements. The iron and calcium elements can be reused as iron-making raw materials, but the sulfur element in the gypsum is required to be removed as it has a harmful effect on the properties of iron. Herein, the influence of carbon and pyrite on the desulfurization behavior of red gypsum is systematically investigated by high-temperature decomposition. In the absence of carbon, a small amount of anhydrite (CaSO4) phase is decomposed after sintering at 1200 °C for 2 h. However, the undesirable oldhamite (CaS) phase is observed in the entombed RG/carbon50 mixture after sintering at 800 °C for 2 h, which implies that a strong reducing atmosphere can promote oldhamite to get generated. Overall, anhydrite decomposition is influenced by the carbon content, sintering temperature, and holding time. In the case of RG/carbon100 mixture, the diffraction peaks of anhydrite are not observed after sintering at 1100 °C for 2 h and 1200 °C for 0.5 h. Moreover, the main phases in RG/carbon100 mixture are found to be gehlenite (Ca2Al(AlSiO7), magnetite (Fe3O4), dicalcium diiron oxide (Ca2Fe2O5), and lime (CaO). In addition, the phase composition of RG/carbon100 mixture is not influenced by the addition of different amounts of pyrite (FeS2) after sintering at 900, 1000, and 1100 °C.