Abstract:Because the disposal of phosphogypsum (PG) can lead to serious contamination of the air, soil, and water, recycling of PG has attracted wide attention. This study investigated the effect and solidification of phosphorus in the production of calcium sulfoaluminate (CSA) cement using PG as the sole CaO source. The effects of three phosphorus impurities (Ca3(PO4)2, CaHPO4, Ca(H2PO4)2) on the decomposition of CaSO4, formation of minerals, microstructure of the clinker, and the hydration and mechanical properties of the cement were studied. Experimental results show that Ca3(PO4)2 and Ca(H2PO4)2 promoted the decomposition of CaSO4 and the formation of clinker minerals with the increase in P2O5 content, whereas CaHPO4 showed a promoting effect only when the P2O5 content was more than 1.5 wt%. The increase in phosphorus incorporation in Ca2SiO4 leads to the transformation of β-Ca2SiO4 to α'-Ca2SiO4 and then to Ca7Si2P2O16. The presence of three phosphates in the clinker enhanced the growth of crystal grains and the generation of a liquid phase. Compared with Ca4Al6SO16 without phosphorus, the hydration reaction of phosphorus-bearing Ca4Al6SO16 started later and ended earlier, and the reaction time was shorter. The presence of phosphorus impurities reduces the 1-day strength of CSA cement but does not affect the development of the 3-day and 28-day strengths. Considering environmental aspects, the solidification of phosphorus in the production of CSA clinker were quantified by measuring the distribution of elements. The results indicated that phosphorus is solidified by Ca4Al6SO16, Ca2SiO4, and Ca4Al2Fe2O10, and Ca2SiO4 has a stronger ability to solidify phosphorus than the other two minerals. Ca3(PO4)2 is more difficult to solidify than CaHPO4 and Ca(H2PO4)2. This study is of great significant to guide the large-scale clean utilization of PG in the production of CSA cement.

Co-preparation of calcium sulfoaluminate cement and sulfuric acid through mass utilization of industrial by-product gypsum

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Properties and Microstructures of 3D Printable Sulphoaluminate Cement Concrete Containing Industrial By-Products and Nano Clay

Recycling phosphogypsum as a sole calcium oxide source in calcium sulfoaluminate cement and its environmental effects

Preparation and 3D printing building application of sulfoaluminate cementitious material using industrial solid waste

Preparation of α-calcium sulfate hemihydrate from industrial by-product gypsum: A review

Progress in the Preparation of Calcium Carbonate by Indirect Mineralization of Industrial By-Product Gypsum

MgO-based supersulfated cement with different industrial by-product gypsum: Experiments and molecular dynamics simulation

Preparation of calcium sulfate from recycled red gypsum to neutralize acidic wastewater and application of high silica residue

Investigation on the preparation of low carbon cement materials from industrial solid waste phosphogypsum: Clinker preparation, cement properties, and hydration mechanism

Experimental Study on Preparation of Calcium Oxide by Coal Reduction of Calcium Sulfate in Carbon Dioxide Atmosphere

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Preparation of Gypsum–Urea with Enhanced Sustainability from Flue Gas Desulfurization Gypsum in Saturated Urea Solution

Preparation and property studies of ferric sulfoaluminate cement based on Bayer red mud and phosphogypsum

Calculation for Mineral Phases in the Calcination of Desulfurization Residue to Produce Sulfoaluminate Cement

Preparation and Properties of a Sulphoaluminate Magnesium-Potassium Phosphate Green Cementitious Composite Material from Industrial Solid Wastes

Preparation of calcium carbonate by indirect carbonation desulfurization gypsum with renewable aspartic acid

Recycling phosphogypsum as the sole calcium oxide source in calcium sulfoaluminate cement production and solidification of phosphorus

Preparing sulfoaluminate cement using phosphogypsum as the only calcium oxide source: Effects of fluoride impurities

Preparation and characterization of cementitious materials based on sulfuric-acid-activated coal gasification coarse slag