Abstract:Huge amount of flue gas desulphurization (FGD) gypsum not only occupies the farmland but also causes severe pollution to the surrounding environment. The most effective way to achieve a high-value utilization of FGD gypsum is to prepare short columnar α-calcium sulfate hemihydrate (α-HH) since short columnar crystals show better mechanical strength than needle-like ones. Here, malic acid, a prolific, inexpensive and environment-friendly modifier was explored for the first time to effectively tune the crystal morphology of α-HH prepared from FGD gypsum in glycerol-water-NaCl solutions. When the concentration of malic acid reached 18.54 × 10-4 mol/kg, α-HH crystals with an average aspect (length-to-diameter) ratio of 1.9 (compared to 29.4 in the absence of malic acid) were prepared. The selective complexation of malic acid with Ca active sites on different α-HH crystal planes played a dominant role in the α-HH crystal morphology transformation, which was then explained by the surface broken bonds theory for the first time. The broken bond number per active Ca atom (Nbper Ca) and broken bond density of Ca atoms (DbCa) on the (2 0 4) end plane were larger than those on the (0 2 0) or (2 0 0) side planes. Therefore, the (2 0 4) end plane was more reactive with organics, resulting in the preferential adsorption of malic acid on the end planes, which reduced the specific surface energy of (2 0 4) and led to an increased exposure of this plane and a decreased exposure of (0 2 0) or (2 0 0) side planes in the final α-HH crystals. Consequently, using malic acid as modifier, the α-HH crystal gradually transformed from a needle-like shape to a short columnar one. This work provided important insights into and perspectives for the selection of crystal modifiers and explanation of the mechanism during the preparation of calcium-containing crystals with controllable morphology.

Preparation of α-High Strength Gypsum from Flue Gas Desulfurization Gypsum Pretreated by Hydrothermal-aging Method

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers: Preparation, simulations, and process analysis

Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste

Pilot scale preparation of α-calcium sulfate hemihydrate from FGD gypsum in Ca–K–Mg aqueous solution under atmospheric pressure

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

α-calcium sulfate hemihydrate preparation from FGD gypsum in recycling mixed salt solutions

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Preparation of CSHW with Flue Gas Desulfurization Gypsum

Preparation of α-CaSO4·½H2O with tunable morphology from flue gas desulphurization gypsum using malic acid as modifier: A theoretical and experimental study

Characterization and Precipitation Mechanism of Α-Calcium Sulfate Hemihydrate Growing out of FGD Gypsum in Salt Solution

Facile preparation of high-strength α-CaSO4·0.5H2O regulated by maleic acid from phosphogypsum: experimental and molecular dynamics simulation studies

Preparation and Performance Study of Alkali-active Gypsum Mixture System

Influence of crystal-transforming agent on the performance and mechanism of α-high-strength gypsum prepared from FGD gypsum

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Facile Preparation of High-Strength Α-Caso 4 ·0.5H 2 O Regulated by Maleic Acid from Phosphogypsum: Experimental and Molecular Dynamics Simulation Studies