Abstract:The excellent matching of strength and toughness with respect to lath martensite is closely related to its hierarchical configuration and crystallographic features. Recently, a few literatures reported that the GreningerTroiano (G-T) relationship, instead of the generally accepted Kurdjumov-Sachs (K-S) relation, was determined in some lath martensite steels. However, the underlying reason is still waiting to be explored. In the present study, systematic characterizations were performed in water-quenched Fe-12Ni-1.5Si-0.2C steel firstly, then a modified version of crystallographic model developed by Morris et al. was proposed to clarify the microstructure and the crystallography with G-T relationship. As the main crystallographic features, the orientation relationship between prior austenite and martensitic variants is close to G-T rather than K-S relation. Further characterization shows that the block interface is parallel to the annealing twin boundary of prior austenite, indicating the {111}gamma habit plane of blocks. Naturally, three crystallographically distinct blocks with {111}gamma interfaces can be configured into a packet with self-accommodation manner to minimize macro strain. In fact, such a hierarchical configuration with G-T relationship can be understood clearly by the modified version of crystallographic model. Firstly, regarding the bivariant block as the basic element which undertakes the invariant plane shear, the total shear strain within each packet region can thus be effectively cancelled out on the common habit planes of {111}gamma due to the self-accommodation effect, leading to an essentially shear strain-free pattern; Secondly, a higher hierarchy is accompanied with a significant decrease of strain and only a homogenous dilation of 0.02 remains in a prior austenite grain, which is closely related to the unique hierarchy; Thirdly, the G-T relationship is natural preferred for the present steel, which satisfies two conditions in this crystallographic model: (i) a minimum of angular deviation between the {111}gamma and the habit plane of bivariant blocks; (ii) three slip systems of dislocations with 111 alpha' Burgers vectors involved during the martensitic transformation, which is also universally observed in the TEM examinations. Besides that, compared with the case of K-S relationship, a potential influence of G-T relationship on mechanical properties may embody in inducing a lower ductile-brittle transition temperature and better toughness of lath martensite steels.

Tetragonality mapping of martensite in a high-carbon steel by EBSD

Mapping of lattice distortion in martensitic steel-Comparison of different evaluation methods of EBSD patterns

High resolution electron backscatter diffraction study on the heterogeneities of tetragonal distortion in Fe-C martensite at the microstructural scale

Study on the Orientational Relationship Between Martensite Variants by EBSD

Crystallographic Analysis of Lath Martensite in a 13Cr-5Ni Steel by Electron Backscattering Diffraction

Influence of Steel Alloying Components on Martensite Tetragonality

Revisiting the Crystallography of {225}γ Martensite: How EBSD Can Help to Solve Long-Standing Controversy

Machine learning informed tetragonal ratio c/a of martensite

The Crystal Structure of As-quenched Fe–C Martensite

Double Diffraction or ω-Fe Diffraction in Body-Centered Cubic {112}<111>-Type Twinned Martensite

The microstructure and crystallography of lath martensite with Greninger-Troiano orientation relationship in a Fe-12.8Ni-1.5Si-0.22% C steel

Texture Analysis of Hot Rolled Martensitic and Bainitic Steels by Electron Backscatter Diffraction to Quantify Parent Austenite States

Crystallography of Martensite in Friction-Stir-Welded 12cr Heat-Resistant Steel

Fine Structure Characterization of Martensite/austenite Constituent in Low‐carbon Low‐alloy Steel by Transmission Electron Forward Scatter Diffraction

Influence of crystallographic texture on Young's modulus of various Alloy 82H welds

Chemical gradients across phase boundaries between martensite and austenite in steel studied by atom probe tomography and simulation

Double Diffraction or -Fe Diffraction in Body-Centered Cubic {112}?111?-Type Twinned Martensite

A crystallographic model of the {557} habit planes in low-carbon martensitic steels

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel

Grain-level effects on in-situ deformation-induced phase transformations in a complex-phase steel using 3DXRD and EBSD

Direct observations of collinear dislocation interaction in a Fe-17.4 Mn-1.50 Al-0.29 C (wt.%) austenitic steel under cyclic loading by in-situ electron channelling contrast imaging and cross-correlation electron backscatter diffraction