Abstract:Cold-drawn pearlitic steel wires have the highest strength of all steel products.It is a promising way to enhance the mechanical properties by increasing the carbon content.However, the proeutectoid cementite forms easily due to the hypereutectoid composition and deteriorates the mechanical and processing properties of steel wires.It is important for hypereutectoid steel wire drawing to achieve a fine and fully pearlitic microstructure without proeutectoid cementite.The austenitization and following continuous cooling process were simulated in the dilatometer for a hypereutectoid steel.The microstructure was observed with OM and SEM.The transformation temperature, prior-austenite grain size, pearlitic interlamellar spacing and proeutectoid cementite thickness were determined by dilatometric curves or OM/SEM images.The austenite grain size increases rapidly with a higher temperature and almost keeps invariant with a longer austenitization time.Faster cooling rate, higher austenitization temperature or longer austenitization time decrease the starting and finishing temperature of phase transformation, widen the temperature range, refine the pearlitic interlamellar spacing and suppress the proeutectoid cementite precipitation (reduce the thickness or make it discontinuous).However, it is easy to form martensite which is bad for the homogeneity of pearlitic microstructure by increasing the cooling rate or austenitization temperature simply.A fine pearlite in a pseudoeutectoid microstructure is achieved by extending the austenitization time to 60 min and controlling the austenitization temperature and cooling rate.Discontinuous proeutectoid cementite is observed in the samples with the higher austenitization temperature.Higher austenitization temperature and longer time are helpful to weaken the carbon concentration gradient.The homogeneous carbon distribution restrains carbon diffusion for cementite nucleation during the proeutectoid cementite precipitation and pearlite

Evolution of Microstructure and Fe/Fe3C Interface Structure in Cold‐Drawn Pearlitic Steel Wires

Cementite Deformation and Dissolution in a Cold-Drawn Pearlitic Steel Wire

Hierarchical Structures in Cold-Drawn Pearlitic Steel Wire

EVOLUTIONS OF MICROSTRUCTURE AND FERRITIC MICRO--ORIENTATION AND TEXTURE IN A PEARLITIC STEEL WIRE DURING COLD DRAWING

Three Distinct Deformation Behaviors of Cementite Lamellae in a Cold-Drawn Pearlitic Wire

Evolution of Cementite Morphology in Pearlitic Steel Wire During Wet Wire Drawing

Characterization of the Microstructure in Drawn Pearlitic Steel Wires

EFFECT OF HEAVILY DRAWING ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Cr ALLOYS

Effect of Microstructure and Microtexture on the Mechanical Properties of Small-Strain Cold-Drawn Pearlite Steel Wires

Microstructure and Properties of Cold Drawing Cu-2.5% Fe-0.2% Cr and Cu-6% Fe Alloys

Study on Dislocation Slips in Ferrite and Deformation of Cementite in Cold Drawn Pearlitic Steel Wires from Medium to High Strain

Relating Residual Stress and Microstructure to Mechanical and Giant Magneto-Impedance Properties in Cold-Drawn Co-based Amorphous Microwires

High deformation and delamination mechanisms explained through mesoscale and nanoscale phenomena in pearlitic steel wires

Microstructural Evolution, Strengthening Mechanisms and Strength Structure Relationship in Cold-Drawn Pearlitic Steel Wire

Microstructural Dependence of Anisotropic Fracture Mechanisms in Cold-Drawn Pearlitic Steels

Influences of Fe Content and Cold Drawing Strain on the Microstructure and Properties of Powder Metallurgy Cu-Fe Alloy Wire

Microstructure Evolution of Cu/Ag Interface in the Cu–6 Wt.% Ag Filamentary Nanocomposite

The Effects of Cold Rolling and Annealing on the Microstructure Evolution of Ordered C-2000 Alloy during Metallic Wire Preparation

Formation and effects of banded structures in 55SiCrA spring steel wire rod

Structure and strength of sub-100 nm lamellar structures in cold-drawn pearlitic steel wire

EFFECTS OF AUSTENITIZATION AND COOLING RATESON THE MICROSTRUCTURE IN A HYPER-EUTECTOID STEEL